POLYMAN® FSAN GF 35 K2405
| Category: | SAN , Styrene Acrylonitrile |
| Manufacturer: | A. Schulman Europe |
| Trademark: | POLYMAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | r5kLhP_POLYMANFSANGF35K2405.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 35% glass fibre reinforced SAN grade for parts with high mechanical strength and high dimensional stability |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.37 | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 220°C/10.0 kg | 7.00 | cm³/10min | ISO 1133 |
| 230°C/3.8 kg | 3.00 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 12000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 100 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 1.3 | % | ISO 527-2/1A/5 |
| Flexural Modulus 1 | 12000 | MPa | ISO 178 |
| Flexural Stress 2(1.7% strain) | 155 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 20 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 97.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 102 | °C | ISO 306/B50 |
| Additional Information |
|---|
| 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom WJ6531LT | Spartech Polycom | PVC Alloy | Spartech |
| ELASTOSIL® R 750/50 | Wacker Chemie AG | Silicone | ELASTOSIL® R |
| Lucofin® 1413-t1 | Lucobit AG | Polyolefin, Unspecified | Lucofin® |
| Osterlene® LLB0918SAH | Osterman & Company | LLDPE | Osterlene® |
| MARPOL® LL4M 812 | Marco Polo International, Inc. | LLDPE | MARPOL® |