Borealis PP EE002AE
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Borealis AG |
| Trademark: | Borealis PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | r5Y8tg_Borealis-PP-EE002AE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EE002AE is a reactor elastomer modified polypropylene intended for injection moulding. The product is available in natural colour. This material has excellent balanced mechanical properties and gives a good surface quality. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.905 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 11 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.5 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 40.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (1.00 mm) | 1100 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 20.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 5.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 1000 | MPa | ISO 178 |
| Flexural Stress | 24.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 7.0 | kJ/m² | ISO 179/1eA |
| -20°C | 9.0 | kJ/m² | ISO 179/1eA |
| 23°C | 65 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU | |
| Notched Izod Impact | ISO 180/1A | ||
| -20°C | 9.0 | kJ/m² | ISO 180/1A |
| 23°C | 55 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 76.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 49.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 135 | °C | ISO 306/A |
| -- | 45.0 | °C | ISO 306/B |
| CLTE - Flow (80°C) | 1.0E-4 | cm/cm/°C | Internal method |
| Melt Energy | 80.0 | kJ/kg | ISO 11357 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 30.0 - 50.0 | °C | |
| Holding Pressure | 30.0 - 60.0 | MPa |
| Injection instructions |
|---|
| Feeding temperature 40 - 80 °CMass temperature 220 - 260 °CBack pressure Low to mediumHolding pressure 30 - 60 barMould temperature 30 - 50 °CScrew speed Low to mediumFlow front speed 100 - 200 m/min |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC M8184 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Shanghai Potomer SG7 | Shanghai Potomer International Trade Co., Ltd. | PVC, Rigid | Shanghai Potomer |
| EVAL™ C109B | EVAL Europe nv | EVOH | EVAL™ |
| Dryflex® 662800S | ELASTO | SEBS | Dryflex® |
| KOCETAL® GF105 | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |