SUMIKASUPER® LCP E6809T
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | Sumitomo Chemical Co., Ltd. |
| Trademark: | SUMIKASUPER® LCP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | r3QvQ5_SUMIKASUPER-LCP-E6809T.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SUMIKASUPER LCP is a thermotropic liquid crystalline polyester, showing the highest heat resistance among engineering plastics. SUMIKASUPER LCP E6809T is a food safety grade which contains an inorganic filler. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.79 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.20 | % | ASTM D955 |
| Transverse flow | 0.65 | % | ASTM D955 |
| Water Absorption (Saturation) | 0.020 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 98.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 5.8 | % | ASTM D638 |
| Flexural Modulus | 10400 | MPa | ASTM D790 |
| Flexural Strength | 111 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact | 450 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 266 | °C | ASTM D648 |
| Additional Information |
|---|
| Mold Shrinkage, Sumitomo Chemical Method, Machine Direction: 2.0 mils/inMold Shrinkage, Sumitomo Chemical Method, Transverse Direction: 6.5 mils/in |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 150 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Regrind | 30 | % | |
| Rear Temperature | 300 - 320 | °C | |
| Middle Temperature | 320 - 350 | °C | |
| Front Temperature | 340 - 370 | °C | |
| Nozzle Temperature | 340 - 370 | °C | |
| Mold Temperature | 70.0 - 160 | °C | |
| Injection Pressure | 78.0 - 157 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 20.0 - 39.0 | MPa | |
| Back Pressure | 0.980 - 4.90 | MPa | |
| Screw Speed | 50 - 100 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SAMAT 5003D1 | POLYROCKS CHEMICAL CO., LTD | PP, Unspecified | SAMAT |
| UBESTA 3035 U | UBE Engineering Plastics, S.A. | Nylon 12 | UBESTA |
| Daelim Po1y® LH7200 | DAELIM INDUSTRIAL CO., LTD. | HDPE | Daelim Po1y® |
| Formolene® 4101O | Formosa Plastics Corporation, U.S.A. | PP Homopolymer | Formolene® |
| SQUARE® SSR3918-40 | Shenzhen SQUARE Silicone Co., Ltd. | Silicone | SQUARE® |