| Vydyne 63H NT0702 is a medium-viscosity, heat-stabilized PA66 resin suitable for injection-molding, extrusion and compounding applications. It is available in natural color only. Vydyne 63H NT0702 resin offers high strength, rigidity and toughness over a broad range of demanding applications, good fluid resistance to a wide variety of chemicals, solvents and oils, and heat stability to ensure property longevity when the material is subjected to higher temperatures. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.14 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Lateral flow : 23°C, 2.00mm | 1.9 | -- | % | ISO 294-4 |
| Traffic : 23°C, 2.00mm | 1.9 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 8.5 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.5 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 3200 | 1700 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | |||
| Yield, 23°C | 85.0 | 55.0 | MPa | ISO 527-2 |
| Fracture, 23°C | 55.0 | 65.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 5.0 | 20 | % | ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) | > 25 | > 200 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2500 | 700 | MPa | ISO 178 |
| Flexural Stress (23°C) | 70.0 | 20.0 | MPa | ISO 178 |
| Poisson's Ratio | 0.40 | -- | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 5.0 | 9.0 | kJ/m² | ISO 179/1eA |
| 23°C | 6.0 | 25 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | No Break | ISO 179/1eU | |
| 23°C | No Break | No Break | ISO 179/1eU | |
| Notched Izod Impact | ISO 180 | |||
| -30°C | 5.0 | 9.0 | kJ/m² | ISO 180 |
| 23°C | 6.0 | 25 | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 190 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 68.0 | -- | °C | ISO 75-2/A |
| Melting Temperature | 260 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 55°C, 2.00mm | 1.0E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C, 2.00mm | 1.0E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Extrusion | Dry | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 250 - 295 | °C | |
| Cylinder Zone 2 Temp. | 250 - 295 | °C | |
| Cylinder Zone 3 Temp. | 250 - 295 | °C | |
| Cylinder Zone 4 Temp. | 250 - 295 | °C | |
| Cylinder Zone 5 Temp. | 250 - 295 | °C | |
| Melt Temperature | 270 - 295 | °C | |
| Die Temperature | 270 - 295 | °C |
| Extrusion instructions |
|---|
| Recommended Extrusion Conditions:Melt Point: 260°CMelt Pressure: 3 to 17 MPaBlow Film Bath Temperature: 20°C to 80°CChill Roll Temperature (Cast Film): 20°C to 80°CScrew Design: General Purpose or Barrier |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PROTEQ™ C18UST5L | Marplex Australia Pty. Ltd. | PP Copolymer | PROTEQ™ |
| RELENE® E 41003 | Reliance Industries Limited | HDPE | RELENE® |
| SureSpec HD54-05 | Genesis Polymers | HDPE, HMW | SureSpec |
| Zhongfa PP FR-08 | Yuyao Zhongfa Engineering Plastics Co. Ltd. | PP, Unspecified | Zhongfa |
| Appeel® 72D799 | DuPont Packaging & Industrial Polymers | EVA | Appeel® |