MEGOLON™ S560UV
| Category: | TP, Unspecified , Thermoplastic |
| Manufacturer: | AlphaGary |
| Trademark: | MEGOLON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | r2QKsu_MEGOLON-S560UV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MEGOLON™ S560UV is a thermoplastic, halogen free, fire retardant cable sheathing compound for general purpose applications. It provides improved resistance to water penetration and absorption compared to conventional halogen free compounds. APPLICATIONS
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.50 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (150°C/21.6 kg) | 7.5 | g/10 min | ISO 1133 |
| Water Absorption | IEC 60811-1-3 | ||
| 10 days : 70°C | 10.0 | g/m² | |
| 30 days : 70°C | 17.0 | g/m² | |
| 90 days : 70°C | 24.0 | g/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Hot Deformation (90°C) | 8.0 | % | BS 6469 99.1 |
| Hot Pressure Test (90°C) | 25 | % | IEC 60811-3-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Acid Gas Emission Conductivity | 7.00 | µS/cm | IEC 60754-2 |
| Acid Gas Emission pH | 6.20 | IEC 60754-2 | |
| Flammability Temperature Index | 290 | °C | ISO 4589-3 |
| Smoke Density | ASTM E662 | ||
| Flaming mode 1 | < 53 | Ds | |
| Non-flaming mode 2 | < 210 | Ds | |
| Toxicity | 0.800 | NES 713 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Halogen Acid Gas Evolution | 0.0 | % | IEC 60754-1 |
| Ozone Resistance | pass | ASTM D470 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Draw Down | 1.5:1.0 | ||
| Extruder Screw Compression Ratio | 1.0:1.0 to 2.0:1.0 |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Mooney Viscosity (ML 1+4, 140°C) | 40 | MU | ASTM D1646 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 55 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | |||
| -- 3 | 14.0 | MPa | IEC 60811-1-2 |
| -- | 10.5 | MPa | IEC 60811-1-1 |
| Tensile Strain | |||
| Break 4 | 140 | % | IEC 60811-1-2 |
| Break | 160 | % | IEC 60811-1-1 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | 8.00 | kN/m | BS 6469 99.1 |
| Aging | Nominal Value | Unit | |
|---|---|---|---|
| Change in Tensile Strength in Air (100°C, 168 hr) | 31 | % | |
| Change in Tensile Strain at Break in Air (100°C, 168 hr) | -11 | % |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 36 | % | ISO 4589-2 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 to 70.0 | °C | |
| Cylinder Zone 1 Temp. | 135 | °C | |
| Cylinder Zone 2 Temp. | 140 | °C | |
| Cylinder Zone 3 Temp. | 145 | °C | |
| Cylinder Zone 4 Temp. | 150 | °C | |
| Cylinder Zone 5 Temp. | 160 | °C | |
| Melt Temperature | 165 to 175 | °C | |
| Die Temperature | 165 | °C |
| Note Message | |
|---|---|
| 1 . | Time to maximum: 7 minutes |
| 2 . | Time to maximum: 3 minutes |
| 3 . | after 7 days at 100°C |
| 4 . | after 7 days at 100°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 6MV14FR4K1681 | A. Schulman Inc. | Nylon 6 | SCHULAMID® |
| THERMOLAST® K TC0GPZ (Series: GP/FG) | KRAIBURG TPE | TPE | THERMOLAST® K |
| TOTAL Polypropylene PPH 4060 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| Carbotex KV-75FD | Kotec Corporation | PC | Carbotex |
| Hax™ HFC 0115/1 | Fainplast Compounds S.r.l | Polyolefin, Unspecified | Hax™ |