Infino GI-3103
| Category: | PC , Polycarbonate |
| Manufacturer: | LOTTE ADVANCED MATERIALS CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | r1epnS_InfinoGI3103.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Infino GI-3103 is a polycarbonate (PC) product that contains a glass fiber reinforced material. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: electrical/electronic applications. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity (Natural) | 1.25 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/10.0 kg) | 33 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.20mm | 0.25 - 0.41 | % | ASTM D955 |
| Transverse flow : 3.20mm | 0.30 - 0.42 | % | ASTM D955 |
| Lateral flow : 3.20mm | 0.30 - 0.42 | % | ISO 2577 |
| Traffic : 3.20mm | 0.25 - 0.41 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 115 | ASTM D785 | |
| R scale | 115 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3200 | MPa | ASTM D638 |
| -- | 3250 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 55.0 | MPa | ASTM D638 |
| Yield | 53.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 59.0 | MPa | ASTM D638 |
| Fracture | 70.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Fracture 4 | 10 | % | ASTM D638 |
| Fracture | 10 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 3100 | MPa | ASTM D790 |
| -- 6 | 3160 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 86.0 | MPa | ASTM D790 |
| -- 8 | 85.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 19 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 230 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 160 | J/m | ASTM D256 |
| 23°C 10 | 18 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 6.40mm | 136 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 4.00mm | 134 | °C | ISO 75-2/B |
| 1.8 MPa, unannealed, 6.40mm | 131 | °C | ASTM D648 |
| 1.8 MPa, not annealed, 4.00mm | 130 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.8 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 5.0 mm/min |
| 6 . | 2.8 mm/min |
| 7 . | 5.0 mm/min |
| 8 . | 2.8 mm/min |
| 9 . | Thickness: 4mm |
| 10 . | Thickness: 4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx FPE3A40CC | The Matrixx Group, Inc. | PE, Unspecified | Matrixx |
| Fainplast PVC MPH 87 | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Hanwha Total PP TH54M | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| MAXATEL® AH100T-NC010 | Pier One Polymers, Inc. | Acetal (POM) Homopolymer | MAXATEL® |
| Hostacom CR 250 F/M C11462 | LyondellBasell Industries | PP Copolymer | Hostacom |