Sarlink® TPE AB-2352D
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | r1dpyv_Sarlink-TPE-AB-2352D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sarlink®TPE AB-2352D is a thermoplastic elastomer (TPE) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is injection molding. Sarlink®The typical application field of TPE AB-2352D is: automobile industry |
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.888 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Vertical flow direction | 1.2 | % | ASTM D955 |
| Flow direction | 1.0 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 57 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 100% Secant | 110 | MPa | ASTM D638 |
| Flexural Modulus | 460 | MPa | ASTM D790 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 15.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 650 | % | ASTM D638 |
| Additional Information |
|---|
| Sarlink® TPE compounds can be processed without drying, but properties may be improved by drying the material for 2 hours at 180°F (82°C). |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 210 - 220 | °C | |
| Middle Temperature | 215 - 225 | °C | |
| Front Temperature | 220 - 230 | °C | |
| Nozzle Temperature | 225 - 235 | °C | |
| Processing (Melt) Temp | 225 - 235 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Pressure | 1.38 - 6.89 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.172 - 0.862 | MPa | |
| Screw Speed | 50 - 120 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| Drying is not necessary. However, if moisture is a problem, dry the pellets for 2 to 4 hours at 150°F (65°C). |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® CLEAR G 830 Rnew MED | Arkema | Nylon 11 | Rilsan® |
| NYLOY® MG-1113B | Nytex Composites Co., Ltd. | Nylon 66 | NYLOY® |
| Globalene® HP560P | Lee Chang Yung Chemical Industry Corp. | PP Homopolymer | Globalene® |
| Kepamid® 1325GF | Korea Engineering Plastics Co., Ltd | Nylon 6 | Kepamid® |
| Kepamid® 2340GM8 | Korea Engineering Plastics Co., Ltd | Nylon 66 | Kepamid® |