Vandar® 2100UV
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Celanese Corporation |
| Trademark: | Vandar® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | r1c6eM_Vandar-2100UV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Vandar 2100UV is a polyester alloy designed to offer maximum impact strength at room and low temperatures. This unfilled compound is characterized by outstanding chemical resistance, dimensional stability, paintability, and toughness. Vandar 2100UV is available in UV stable colors. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.23 | g/cm³ | ASTM D792 |
| -- | 1.22 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (250°C/5.0 kg) | 5.50 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow | 1.8 | % | ASTM D955 |
| Vertical flow direction | 1.7 - 2.2 | % | ISO 294-4 |
| Flow direction | 1.7 - 2.2 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.20 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 38 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1760 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Yield, 23°C | 43.4 | MPa | ASTM D638 |
| Yield | 38.0 | MPa | ISO 527-2/1A/50 |
| Fracture | 29.0 | MPa | ISO 527-2/1A/50 |
| 50% strain | 26.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain | |||
| Yield | 4.4 | % | ISO 527-2/1A/50 |
| Fracture, 23°C | 150 | % | ASTM D638 |
| Fracture | 250 | % | ISO 527-2/1A/50 |
| Nominal Tensile Strain at Break | 170 | % | ISO 527-2/1A/50 |
| Flexural Modulus (23°C) | 1670 | MPa | ISO 178 |
| Flexural Stress (23°C) | 47.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 19 | kJ/m² | ISO 179/1eA |
| 23°C | 80 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU | |
| Notched Izod Impact (23°C) | No Break | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 86.0 | °C | ISO 75-2/B |
| 0.45 MPa, annealed | 104 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 48.9 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 51.0 | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 60.0 | °C | ISO 11357-2 |
| Vicat Softening Temperature | 128 | °C | ISO 306/B50 |
| Melting Temperature 2 | 225 | °C | ISO 11357-3, ASTM D3418 |
| CLTE - Flow | 1.3E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| Dielectric Strength | 24 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 4.00 | IEC 60250 | |
| 1 MHz | 3.60 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 7.0E-3 | IEC 60250 | |
| 1 MHz | 0.020 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 130 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Max Regrind | 25 | % | |
| Hopper Temperature | 20.0 - 50.0 | °C | |
| Rear Temperature | 230 - 240 | °C | |
| Middle Temperature | 235 - 250 | °C | |
| Front Temperature | 235 - 250 | °C | |
| Nozzle Temperature | 240 - 260 | °C | |
| Processing (Melt) Temp | 235 - 260 | °C | |
| Mold Temperature | 65.0 - 96.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.00 - 0.345 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 250 to 260°CZone 4 Temperature: 240 to 260°CFeed Temperature: 230 to 240°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Thermoplastic Polyolefin FT4702-00 | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| Teflon® FEP 9495 | DuPont Fluoropolymers | FEP | Teflon® FEP |
| Akulon® F130-C3 | DSM Engineering Plastics | Nylon 6 | Akulon® |
| Lupoy® SC1004AU | LG Chem Ltd. | PC | Lupoy® |
| Plaslube® PC / ABS EP | Techmer Engineered Solutions | PC+ABS | Plaslube® |