Alathon® M6010-2
| Category: | HDPE, MMW , High Density (MMW) Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Alathon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | r1KbTQ_AlathonM60102.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Alathon M6010-2 is a medium molecular weight high density polyethylene homopolymer for use in blown film applications. Typical applications include those with low WVTR requirements. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.958 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.2 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM E111 | ||
| MD : 32 µm, blown film | 993 | MPa | ASTM E111 |
| TD : 32 µm, blown film | 1320 | MPa | ASTM E111 |
| Tensile Strength | |||
| MD : Yield, 32 µm, blown film | 31.0 | MPa | ASTM D882 |
| TD : Yield, 32 µm, blown film | 34.5 | MPa | ASTM E111 |
| MD : Broken, 32 µm, blown film | 57.2 | MPa | ASTM D882 |
| TD : Broken, 32 µm, blown film | 31.0 | MPa | ASTM D882 |
| Tensile Elongation - MD (Broken, 32 µm, blown film) | 650 | % | ASTM D882 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 32 µm, blown film | 19 | g | ASTM D1922 |
| TD : 32 µm, blown film | 550 | g | ASTM D1922 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stanyl® TS272A1 | DSM Engineering Plastics | Nylon 46 | Stanyl® |
| ULTEM™ HU2100 resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| Cheng Yu C6600 | Cheng Yu Plastic Company Limited | PC+ABS | Cheng Yu |
| Ecobarrier® 0625 | Noble Polymers | Polyolefin, Unspecified | Ecobarrier® |
| Karina RED COLOR CONCNETRATE 42/155-RG-GE (CS) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |