LUBEMID B27 GK30 NATURAL
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LUBEN PLAST srl |
| Trademark: | LUBEMID |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qygl54_LUBEMID-B27-GK30-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Compound based on PA6 natural first choice. With glass beads 30%. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.33 to 1.37 | g/cm³ | ISO 1183/A |
| Water Absorption (23°C, 24 hr, 3.20 mm) | 1.4 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3500 to 4200 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | ISO 527-2/1A/5 | ||
| Yield | 45.0 to 50.0 | MPa | |
| Break | 40.0 to 45.0 | MPa | |
| Tensile Strain | ISO 527-2/1A/5 | ||
| Yield | 3.0 to 4.0 | % | |
| Break | 6.0 to 8.0 | % | |
| Flexural Modulus 1 | 2700 to 3300 | MPa | ISO 178 |
| Flexural Stress 2 | 80.0 to 90.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.0 to 4.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 25 to 35 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | |||
| 23°C, 3.20 mm | 40 to 50 | J/m | ASTM D256A |
| 23°C 3 | 30 to 40 | kJ/m² | ASTM D256 |
| 23°C | 3.0 to 5.0 | kJ/m² | ISO 180/A |
| 23°C 4 | 4.0 to 5.0 | kJ/m² | ASTM D256 |
| Unnotched Izod Impact Strength (23°C) | 25 to 35 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 190 to 200 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 190 to 200 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 3.20 mm | 50.0 to 60.0 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 200 to 210 | °C | ISO 306/A120 |
| -- | 190 to 200 | °C | ISO 306/B120 |
| Melting Temperature | 210 to 225 | °C | Internal Method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index (2.00 mm) | 650 | °C | IEC 60695-2-12 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Notch E |
| 4 . | Notch A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wellamid® MRGF25/15 42H-BK848 (Interior) | Wellman Engineering Resins | Nylon 6 | Wellamid® |
| Zhongfa PP ZF-YM | Yuyao Zhongfa Engineering Plastics Co. Ltd. | PP, Unspecified | Zhongfa |
| FERROFLO® SPS20PK11WH | Ferro Corporation | PS (HIPS) | FERROFLO® |
| Hanwha Total PE E153F | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | EVA | Hanwha Total PE |
| Hostacom M2 R03 | LyondellBasell Industries | PP Copolymer | Hostacom |