ULTEM™ AUT195 resin
| Category: | PEI+PCE , Polyether Imide + PCE |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qxKRML_ULTEM-AUT195-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High flow Polyetherimide blend for automotive lighting applications where highly metallized, reflective surfaces are required. Haze onset temperature of 195C (SABIC test method). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.26 | g/cm³ | ASTM D792 |
| -- | 1.27 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (337°C/6.6 kg) | 24 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (340°C/5.0 kg) | 16.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.50 to 0.70 | % | |
| Across Flow 1 | 0.50 to 0.70 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.90 | % | |
| Equilibrium, 23°C, 50% RH | 0.50 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3000 | MPa | ISO 527-2/1 |
| Tensile Strength 2(Yield) | 96.5 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 70 | % | ASTM D638 |
| Flexural Modulus | |||
| 100 mm Span 4 | 3170 | MPa | ASTM D790 |
| -- 5 | 3100 | MPa | ISO 178 |
| Flexural Strength 6(Yield, 100 mm Span) | 145 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 7 | ISO 179/1eA | ||
| -30°C | 4.0 | kJ/m² | |
| 23°C | 4.0 | kJ/m² | |
| Notched Izod Impact | |||
| 23°C | 53 | J/m | ASTM D256 |
| -30°C 8 | 5.0 | kJ/m² | ISO 180/1A |
| 23°C 9 | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | 2100 | J/m | ASTM D4812 |
| Reverse Notch Izod Impact (3.20 mm) | 2100 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed, 100 mm Span 10 | 195 | °C | ISO 75-2/Be |
| 1.8 MPa, Unannealed, 6.40 mm | 190 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 100 mm Span 11 | 180 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | 205 | °C | ISO 306/B120 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 150°C | 6.0E-5 | cm/cm/°C | |
| Transverse : 23 to 150°C | 6.0E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.23 | W/m/K | ISO 8302 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Metallized Haze Onset | 195 | °C | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 130 to 140 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Hopper Temperature | 80.0 to 100 | °C | |
| Rear Temperature | 320 to 340 | °C | |
| Middle Temperature | 330 to 350 | °C | |
| Front Temperature | 340 to 360 | °C | |
| Nozzle Temperature | 340 to 360 | °C | |
| Processing (Melt) Temp | 340 to 380 | °C | |
| Mold Temperature | 125 to 140 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 2.6 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 2.6 mm/min |
| 7 . | 80*10*4 sp=62mm |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 120*10*4 mm |
| 11 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP ESD C 780 | RTP Company | HDPE | RTP |
| Electrafil® PA6 CF30 TL10 | Techmer Engineered Solutions | Nylon 6 | Electrafil® |
| Estane® 2103-90AEL TPU | Lubrizol Advanced Materials, Inc. | TPU-Polyether | Estane® |
| TOTAL Polyethylene Lumicene® M 4043 UV (EU) | TOTAL Refining & Chemicals | mMDPE | TOTAL Polyethylene |
| Trilliant™ HC 2020-0001 FR | PolyOne Corporation | Copolyester | Trilliant™ HC |