PALSAFE®R 05 GF 20 FR 0 is a polycarbonate (PC) product containing a 20% glass fiber reinforced material. It can be processed by injection molding and is available in Europe. Typical application areas are: electrical/electronic applications. Features include: flame retardant/rated flame Flame Retardant High stiffness high strength high viscosity

General Information
Filler / Reinforcement	Glass fiber reinforced material, 20% filler by weight
Features	Rigidity, high High strength Viscosity, High Flame retardancy
Uses	Electrical/Electronic Applications
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Density	1.35	g/cm³	ISO 1183
Water Absorption			ISO 62
Saturated, 23°C	0.28	%	ISO 62
Equilibrium, 23°C, 50% RH	0.14	%	ISO 62

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	6000	MPa	ISO 527-2/1A/1
Tensile Stress (Break, 23°C)	95.0	MPa	ISO 527-2/1A/5
Tensile Strain (Break, 23°C)	2.5	%	ISO 527-2/1A/5

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	148	°C	ISO 306/B50

Electrical	Nominal Value	Unit	Test Method
Comparative Tracking Index (Solution A)	175	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flame Rating (1.60 mm)	V-0		UL 94

Additional Information
Tensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 5500 to 6500 MPaTensile Stress at Break, ISO 527, 23°C, 5 mm/min, Type A: 90 to 100 MPaTensile Strain at Break, ISO 527, 23°C, 5 mm/min, Type A: 2 to 3 %Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 146 to 149 °CDensity, ISO 1183: 1.34 to 1.36 g/cm³Water Absorption, ISO 62, 23°C, Saturation: 0.25 to 0.3 %Moisture Absorption, ISO 62, 23°C, 50% RH: 0.12 to 0.15 %

Additional Information

Tensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 5500 to 6500 MPaTensile Stress at Break, ISO 527, 23°C, 5 mm/min, Type A: 90 to 100 MPaTensile Strain at Break, ISO 527, 23°C, 5 mm/min, Type A: 2 to 3 %Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 146 to 149 °CDensity, ISO 1183: 1.34 to 1.36 g/cm³Water Absorption, ISO 62, 23°C, Saturation: 0.25 to 0.3 %Moisture Absorption, ISO 62, 23°C, 50% RH: 0.12 to 0.15 %

Resin Grade	Manufacturer	Category	Trademark
Bapolan® 6055	Bamberger Polymers, Inc.	PS (GPPS)	Bapolan®
DOMAMID® 27	DOMO Caproleuna GmbH	Nylon 6	DOMAMID®
Elastron® D D401.A60.N	Elastron USA, Inc.	SBS	Elastron® D
Karina CLEAR PVC COMPOUND 800-204-IS-RG	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
Karina IVORY PVC COMPOUND 900-35/2-P-IS	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina