DIC.PPS CZL-5000
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | DIC Corporation |
| Trademark: | DIC.PPS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qvkhU9_DIC-PPS-CZL-5000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| DIC.PPS CZL-5000 is a polyphenylene sulfide (PPS) product that contains carbon \ptfe. It can be processed by injection molding and is available in North America or Asia Pacific. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.69 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.25 | % | ASTM D955 |
| Transverse flow | 1.0 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.050 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| Class m | 98 | ASTM D785 | |
| Class r | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 15000 | MPa | ASTM D638 |
| Tensile Strength | 90.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 0.60 | % | ASTM D638 |
| Flexural Modulus | 14000 | MPa | ASTM D790 |
| Flexural Strength | 120 | MPa | ASTM D790 |
| Compressive Strength | 120 | MPa | ASTM D695 |
| Coefficient of Friction | ASTM D1894 | ||
| With Metal-Dynamic | 0.20 | ASTM D1894 | |
| With metal-static | 0.20 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 50 | J/m | ASTM D256 |
| Unnotched Izod Impact | 150 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 265 | °C | ASTM D648 |
| CLTE - Flow (-30 to 100°C) | 1.2E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 |
| Additional Information |
|---|
| Flexural Elongation @ Break, ASTM D790: 1% |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 300 - 340 | °C | |
| Middle Temperature | 300 - 340 | °C | |
| Front Temperature | 300 - 340 | °C | |
| Mold Temperature | 120 - 150 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC P6180A | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Vinnolit® PA 5470/5 | Vinnolit GmbH & Co. KG | PVC Homopolymer | Vinnolit® |
| Adell PP ER-19 | Adell Plastics, Inc. | PP Homopolymer | Adell PP |
| Ferro PP LPP20BK88HB | Ferro Corporation | PP, Unspecified | Ferro PP |
| Sylvin 9710-80FUV Red 6228 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |