VECTRA® S540
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | VECTRA® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | quQiyw_VECTRA-S540.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
40% mineral filled grade, low warpage high flow. Chemical abbreviation according to ISO 1043-1 : LCP Inherently flame retardant FDA compliant UL-Listing V-0 in natural and black at .4mm thickness per UL 94 flame testing. UL = Underwriters Laboratories (USA) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.74 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 0.90 | % | ISO 294-4 |
| Flow direction | 0.10 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 3.0E-3 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7500 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 100 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2/1A/50 |
| Flexural Modulus (23°C) | 9200 | MPa | ISO 178 |
| Flexural Stress (23°C) | 130 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 13 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 3.5 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 13 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 275 | °C | ISO 75-2/A |
| Melting Temperature 1 | 350 | °C | ISO 11357-3 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 6.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Hopper Temperature | 20.0 - 40.0 | °C | |
| Rear Temperature | 345 - 355 | °C | |
| Middle Temperature | 355 - 365 | °C | |
| Front Temperature | 365 - 375 | °C | |
| Nozzle Temperature | 365 - 375 | °C | |
| Processing (Melt) Temp | 365 - 375 | °C | |
| Mold Temperature | 80.0 - 140 | °C | |
| Injection Pressure | 50.0 - 150 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 50.0 - 150 | MPa | |
| Back Pressure | 0.00 - 3.00 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 365 to 375°CZone 4 Temperature: 365 to 375°CFeed Temperature: 60 to 80°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2102 TFE 10 | RTP Company | PEI | RTP |
| NEFTEKHIM PP 4270G | Nizhnekamskneftekhim Inc. | PP Copolymer | NEFTEKHIM PP |
| ColorRx® POM1-2000RX | LTL Color Compounders, Inc. | Acetal (POM) Homopolymer | ColorRx® |
| Colorite CS Series CS9034SR | Colorite Polymers | PVC, Flexible | Colorite CS Series |
| Latishield 66-13A G/30 | LATI S.p.A. | Nylon 66 | Latishield |