POLYFLAM® RMMB 40300
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | A. Schulman Europe |
| Trademark: | POLYFLAM® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qthn0U_POLYFLAM-RMMB-40300.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Flame retardant ABS/PC blend; halogen free according to DIN VDE 0472 part 815 |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.17 | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 60.0 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2800 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 63.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 4.0 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 12 | kJ/m² | ISO 179/1eA |
| 23°C | 18 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 118 | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 84.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 105 | °C | ISO 306/A50 |
| -- | 100 | °C | ISO 306/B50 |
| Ball Pressure Test (90°C) | Pass | IEC 60695-10-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+13 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 575 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | ISO 3795 | ||
| 1.50mm, automatic fire extinguishing | 0.0 | mm/min | ISO 3795 |
| 3.00mm, automatic fire extinguishing | 0.0 | mm/min | ISO 3795 |
| Flame Rating | |||
| 1.50 mm | V-0 | UL 94, IEC 60695-11-10, -20 | |
| 3.00 mm | V-0 5V | UL 94 | |
| 3.00 mm | V-0 5VA 5VB | IEC 60695-11-10, -20 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.50 mm | 960 | °C | IEC 60695-2-12 |
| 3.00 mm | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.50 mm | 775 | °C | IEC 60695-2-13 |
| 3.00 mm | 775 | °C | IEC 60695-2-13 |
| Oxygen Index | 29 | % | ISO 4589-2 |
| Additional Information |
|---|
| 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 250 | °C | |
| Middle Temperature | 270 | °C | |
| Front Temperature | 270 | °C | |
| Nozzle Temperature | 280 | °C | |
| Processing (Melt) Temp | 250 - 280 | °C | |
| Mold Temperature | 60.0 - 80.0 | °C | |
| Injection Pressure | 80.0 - 150 | MPa | |
| Injection Rate | Slow-Moderate | ||
| Holding Pressure | 30.0 - 70.0 | MPa | |
| Back Pressure | 5.00 - 10.0 | MPa | |
| Cushion | < 5.00 | mm | |
| Screw Speed | mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYPRO® 5014L SL205 | YUHWA Korea Petrochemical Ind. Co., Ltd. | PP Homopolymer | POLYPRO® |
| FHR Polypropylene P4G4Z-011 | Flint Hills Resources, LP | PP Homopolymer | FHR Polypropylene |
| Jampilen HP502R | Jam Polypropylene Company | PP Homopolymer | Jampilen |
| Jiangsu Sinarise JM8211U | Jiangsu Sinarise New Material Technology Co., Ltd | TPE | Jiangsu Sinarise |
| Sylvin 3280-65 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |