VENYL SW108 - 7838
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | AD majoris |
| Trademark: | VENYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qsvmHZ_VENYL-SW108---7838.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VENYL SW108 - 7838 is a 15 % glass bead reinforced polyamide 6 intended for Injection moulding. APPLICATIONS VENYL SW108 - 7838 has been developed especially for very demanding applications in automotive industry and electrical parts requiring excellent combination between thermal and mechanical properties, good surface finish and good compression strength. VENYL SW108 - 7838 is available grey but other colours can be provided on request. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.25 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.60 to 1.2 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.5 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3500 | 1150 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 80.0 | 52.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 30 | 120 | % | ISO 527-2 |
| Flexural Modulus | 3150 | 1000 | MPa | ISO 178 |
| Flexural Stress | 138 | 72.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 4.7 | 26 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | No Break | No Break | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 180 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 130 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 220 | -- | °C | ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+11 | ohms | DIN 53482 |
| Volume Resistivity | 1.0E+14 | 1.0E+12 | ohms·cm | DIN 53482 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 265 to 280 | °C | |
| Middle Temperature | 255 to 270 | °C | |
| Front Temperature | 255 to 270 | °C | |
| Nozzle Temperature | 240 to 275 | °C | |
| Mold Temperature | 60.0 to 100 | °C | |
| Injection Pressure | 60.0 to 90.0 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 50.0 to 70.0 | MPa | |
| Screw L/D Ratio | 15.0:1.0 to 20.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SRF3707 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| TRAMID® 4110G40 | Samyang Corporation | Nylon, Unspecified | TRAMID® |
| VAMPAMID 66 3530 V0 P | Vamp Tech | Nylon 66 | VAMPAMID |
| Karina IVORY PVC COMPOUND 650-35/1-F | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Durethan® BC 304 000000 | LANXESS GmbH | Nylon 6 | Durethan® |