Skyrol® SH71S
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | SKC Inc. |
| Trademark: | Skyrol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qsigUg_Skyrol-SH71S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Skyrol® SH71S is an optically clear polyester film with high clarity, smooth surface, high gloss, and good dimensional stability. SH71S is slip-treated on one side for good handling characteristics. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 1.40 | g/cm³ | ASTM D1505 |
| Molding Shrinkage | Internal Method | ||
| Flow : 150°C, 30 min, 0.0500 mm | 1.2 | % | |
| Flow : 150°C, 30 min, 0.100 mm | 1.1 | % | |
| Across Flow : 150°C, 30 min, 0.0500 mm | 0.50 | % | |
| Across Flow : 150°C, 30 min, 0.100 mm | 0.60 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic 2 | 0.40 | ||
| vs. Itself - Dynamic 3 | 0.40 | ||
| vs. Itself - Static 4 | 0.50 | ||
| vs. Itself - Static 5 | 0.40 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 50 µm | 207 | MPa | |
| MD : Yield, 100 µm | 193 | MPa | |
| TD : Yield, 50 µm | 234 | MPa | |
| TD : Yield, 100 µm | 214 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 50 µm | 160 | % | |
| MD : Break, 100 µm | 180 | % | |
| TD : Break, 50 µm | 120 | % | |
| TD : Break, 100 µm | 130 | % |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gardner Gloss | ASTM D523 | ||
| 50.0 µm | 191 | ||
| 100 µm | 187 | ||
| Transmittance | ASTM D1003 | ||
| 50.0 µm | 89.0 | % | |
| 100 µm | 89.0 | % | |
| Haze | ASTM D1003 | ||
| 50.0 µm | 0.80 | % | |
| 100 µm | 1.1 | % |
| Note Message | |
|---|---|
| 1 . | 50 µm |
| 2 . | 50 µm |
| 3 . | 100 µm |
| 4 . | 50 µm |
| 5 . | 100 µm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polypropylene PPC 6742 | TOTAL Refining & Chemicals | PP Impact Copolymer | TOTAL Polypropylene |
| Beamset 577 | Arakawa Chemical Industries, Ltd. | PUR, Unspecified | Beamset |
| Karina RED PVC COMPOUND 701D42/266-SD | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina NATURAL PVC COMPOUND 70900-25/ 1-E-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ LUBRICOMP™ Noryl_SPN422L compound | SABIC Innovative Plastics | PPE+PS | LNP™ LUBRICOMP™ |