LEXAN™ LUX7636C resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qsBTLQ_LEXANLUX7636Cresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LEXAN LUX7636C Polycarbonate (PC) resin is a non-filled, extrudable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 1.0 mm / 5VA rating at 3.0mm and is UV stabilized(F1 rating) providing additional weathering capability. LEXAN LUX7636C is available in diffusion colors. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.19 | g/cm³ | ASTM D792 |
| -- | 1.20 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 5.0 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 5.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Flow : 3.20mm | 0.55 - 0.75 | % | Internal method |
| Transverse flow : 3.20mm | 0.60 - 0.80 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.14 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.11 | % | ISO 62 |
| Outdoor Suitability | f1 | UL 746C |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2500 | MPa | ASTM D638 |
| -- | 2400 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 68.0 | MPa | ASTM D638 |
| Yield | 67.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 52.0 | MPa | ASTM D638 |
| Fracture | 52.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 6.0 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2/50 |
| Fracture 5 | 51 | % | ASTM D638 |
| Fracture | 23 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 6 | 2400 | MPa | ASTM D790 |
| -- 7 | 2500 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 103 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 106 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9 | ISO 179/1eA | ||
| -30°C | 9.0 | kJ/m² | ISO 179/1eA |
| 23°C | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 10 | ISO 179/1eU | ||
| -30°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU | |
| Notched Izod Impact | |||
| -30°C | 85 | J/m | ASTM D256 |
| 23°C | 100 | J/m | ASTM D256 |
| -30°C 11 | 9.0 | kJ/m² | ISO 180/1A |
| 23°C 12 | 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | ASTM D4812, ISO 180/1U | ||
| -30°C | No Break | ASTM D4812, ISO 180/1U | |
| 23°C | No Break | ASTM D4812, ISO 180/1U | |
| Instrumented Dart Impact (23°C, Total Energy) | 66.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 131 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 100 mm span 13 | 131 | °C | ISO 75-2/Be |
| 1.8 MPa, unannealed, 3.20mm | 120 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 100 mm span 14 | 120 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 136 | °C | ASTM D1525 15 |
| -- | 137 | °C | ISO 306/B50 |
| -- | 139 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 6.6E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 80°C | 7.2E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 7.0E-5 | cm/cm/°C | ASTM E831 |
| Lateral : 23 to 80°C | 7.6E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Elec | 125 | °C | UL 746 |
| RTI Imp | 120 | °C | UL 746 |
| RTI | 125 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Constant (1.10 GHz) | 2.79 | ASTM ES7-83 | |
| Dissipation Factor (1.10 GHz) | 5.8E-3 | ASTM ES7-83 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.400 mm | V-2 | UL 94 | |
| 1.00 mm | V-0 | UL 94 | |
| 3.00 mm | 5VA | UL 94 | |
| Glow Wire Flammability Index (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.00 mm) | 875 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 60 | % | |
| Rear Temperature | 266 - 288 | °C | |
| Middle Temperature | 277 - 299 | °C | |
| Front Temperature | 288 - 310 | °C | |
| Nozzle Temperature | 282 - 304 | °C | |
| Processing (Melt) Temp | 288 - 310 | °C | |
| Mold Temperature | 71.1 - 93.3 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Vent Depth | 0.025 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*3 sp=62mm |
| 10 . | 80*10*3 sp=62mm |
| 11 . | 80*10*3 |
| 12 . | 80*10*3 |
| 13 . | 120*10*4 mm |
| 14 . | 120*10*4 mm |
| 15 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen EP540V | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| Axiall PVC 8765 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Jam HDPE HF7750M2 | Jam Petrochemical Company | HDPE | Jam HDPE |
| Plasmer 9170B/8901 | HYUNDAI EP Co., Ltd. | TPE | Plasmer |
| Sylvin 916VO-85C Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |