MAJORIS AE267 - 8229
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qrvwn0_MAJORIS-AE267---8229.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AE267 - 8229 is a black mineral filled, low melt flow rate polypropylene copolymer with a good stiffness, a very high level of impact strength and UV stabilized . APPLICATIONS AE267 - 8229 is recommended for the extrusion of profiles (building, electrical, furniture and construction profiles or pipes). Products made from this material show a high dimensional stability and low process shrinkage. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.60 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2290 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 25.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 130 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 34 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Cylinder Zone 1 Temp. | 190 to 230 | °C | |
| Cylinder Zone 3 Temp. | 190 to 230 | °C | |
| Cylinder Zone 5 Temp. | 190 to 230 | °C | |
| Melt Temperature | 200 to 230 | °C | |
| Head Temperature | 200 to 230 | °C | |
| Die Temperature | 200 to 230 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ADEKA EP-4100HF | Adeka Corporation | Epoxy | ADEKA |
| Chemical Resources PP 3700 | Chemical Resources, Inc. | PP Homopolymer | Chemical Resources |
| Crastin® HR5315HF BK503 | DuPont Performance Polymers | PBT | Crastin® |
| Kepital® F25-03 | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |
| Loyblend® TA-1005 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PC+ABS | Loyblend® |