VALOX™ 430 resin
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qpNoCo_VALOX430resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 33 % glass reinforced, impact modified. Connectors, etc. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.52 | g/cm³ | ASTM D792 |
| Specific Volume | 0.650 | cm³/g | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 12 | g/10 min | ASTM D1238 |
| Molding Shrinkage | Internal method | ||
| Flow 1 | 0.30 - 0.50 | % | Internal method |
| Flow 2 | 0.50 - 0.80 | % | Internal method |
| Flow : 3.20mm | 0.50 | % | Internal method |
| Transverse flow 3 | 0.40 - 0.60 | % | Internal method |
| Transverse flow 4 | 0.60 - 0.90 | % | Internal method |
| Water Absorption (24 hr) | 0.050 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 125 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 5 | 8670 | MPa | ASTM D638 |
| Tensile Strength 6(Break) | 106 | MPa | ASTM D638 |
| Tensile Elongation 7(Break) | 3.1 | % | ASTM D638 |
| Flexural Modulus 8(50.0 mm Span) | 7810 | MPa | ASTM D790 |
| Flexural Strength 9(Break, 50.0 mm Span) | 174 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 130 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 860 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 223 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 208 | °C | ASTM D648 |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 130 | °C | UL 746 |
| RTI | 140 | °C | UL 746 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Arc Resistance 10 | PLC 5 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 1 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 2 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 0 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 0 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.47 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 12 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 80 | % | |
| Rear Temperature | 238 - 254 | °C | |
| Middle Temperature | 243 - 260 | °C | |
| Front Temperature | 249 - 266 | °C | |
| Nozzle Temperature | 243 - 260 | °C | |
| Processing (Melt) Temp | 249 - 266 | °C | |
| Mold Temperature | 65.6 - 87.8 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 50 - 80 | rpm | |
| Vent Depth | 0.025 - 0.038 | mm |
| Note Message | |
|---|---|
| 1 . | 1.5 to 3.2 mm |
| 2 . | 3.2 to 4.6 mm |
| 3 . | 1.5 to 3.2 mm |
| 4 . | 3.2-4.6 mm |
| 5 . | 5.0 mm/min |
| 6 . | Type 1, 5.0 mm/min |
| 7 . | Type 1, 5.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | Tungsten electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYTROPE® TPP 518 | A. Schulman Inc. | TPO (POE) | POLYTROPE® |
| Sylvin RP 3504 White | Sylvin Technologies Incorporated | PVC, Rigid | Sylvin |
| THERMOLAST® K TC9FLZ (Series: FR/AP) | KRAIBURG TPE | TPE | THERMOLAST® K |
| CERTENE™ PBM-12AN | Muehlstein | PP Impact Copolymer | CERTENE™ |
| HAIPLEN EP50 C8 | Taro Plast S.p.A. | PP Copolymer | HAIPLEN |