Ultramid® HFX 32 BK00464
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qnkyFx_UltramidHFX32BK00464.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid HFX 32 BK00464 is a polyamide specialty extrusion resin combining high flexibility, excellent burst performance and outstanding chemical resistance. It offers high melt strength and enhanced heat stability. Applications Ultramid HFX 32 BK00464 is recommended for tubing applications requiring an outstanding balance of flexibility, chemical and heat resistance and burst performance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.03 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 490 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 33.0 | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) | 240 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 450 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 120 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 90 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 40.0 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 220 | °C | ISO 3146 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Cylinder Zone 1 Temp. | 225 - 245 | °C | |
| Cylinder Zone 3 Temp. | 225 - 250 | °C | |
| Cylinder Zone 5 Temp. | 225 - 245 | °C | |
| Flange temperature | 230 - 245 | °C | |
| Head Temperature | 230 - 245 | °C | |
| Extruder Screw L/D Ratio | 20.0:1.0 to 24.0:1.0 | ||
| Extruder Screw Compression Ratio | 3.5:1.0 to 4.0:1.0 | ||
| Melt Temperature | 225 - 245 | °C | |
| Die Temperature | 230 - 245 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEREZ ABS 3016 | TER HELL PLASTIC GMBH | ABS | TEREZ ABS |
| Beamset 710 | Arakawa Chemical Industries, Ltd. | Acrylic, Unspecified | Beamset |
| Comai 728-1 UV | Comai Ltda | LLDPE | Comai |
| FHR EPS 55-5655 | Flint Hills Resources, LP | PS (EPS) | FHR EPS |
| Karina IVORY PVC COMPOUND 802D35/ 1-E-AC-LF | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |