RIALFLAME H V0HF 15 S
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | RIALTI Srl |
| Trademark: | RIALFLAME |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qmIoqd_RIALFLAME-H-V0HF-15-S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polyproplene homopolymer compound flame retardanted; classifiable, according to the norms of UL94, V0 up to 1.5mm. Totally halogen and heavy metals free, excellent properties of flame reaction with few emission of smoke at low density and opacity. Good impact strength and general properties, high flowability for injection molding in applications for the electric and electronic field. Available in natural version and colored as per sample. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.5 | % | |
| Flow | 1.5 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 77 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/20 | ||
| Yield, 23°C | 30.0 | MPa | |
| Break, 23°C | 21.0 | MPa | |
| Tensile Strain | ISO 527-2/20 | ||
| Yield, 23°C | 3.0 | % | |
| Break, 23°C | 21 | % | |
| Flexural Modulus 1(23°C) | 2700 | MPa | ISO 178 |
| Flexural Stress (23°C) | 48.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 20 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength (23°C) | 2.3 | kJ/m² | ISO 180/1A |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Accelerated Oven Aging (150°C) | 6.3 | day | ISO 4577 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Needle Flame Test 2(2.00 mm) | Pass | IEC 60695-2-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 62.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 95.0 | °C | ISO 306/B50 |
| Ball Pressure Test (125°C) | Pass | IEC 335 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 2.00 mm | 960 | °C | |
| 4.00 mm | 960 | °C | |
| Glow Wire Ignition Temperature (2.00 mm) | 775 | °C | IEC 60695-2-13 |
| Oxygen Index | 32 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 180 to 200 | °C | |
| Mold Temperature | 30.0 to 40.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | Method A-B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polytron® A30N02 | Polyram Ram-On Industries | Nylon 66 | Polytron® |
| Vydyne® R533H BK0667 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| Borstar® FB2310 | Borealis AG | LLDPE | Borstar® |
| Arnite® T06 202 XL | DSM Engineering Plastics | PBT | Arnite® |
| Jampilen RP316M | Jam Polypropylene Company | PP Random Copolymer | Jampilen |