PRL PPX-FR2
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qm4gA0_PRL-PPX-FR2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRL PPX-FR2 is a Polyphenylene Ether + PS (PPE+PS) product. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.09 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/11.6 kg) | 20 to 40 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 3.18 mm | 0.50 to 0.70 | % | |
| Across Flow : 3.18 mm | 0.50 to 0.70 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18 mm | 56.5 | MPa | |
| Break, 3.18 mm | 49.0 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield, 3.18 mm | 6.0 | % | |
| Break, 3.18 mm | 25 | % | |
| Flexural Modulus (3.18 mm) | 2410 | MPa | ASTM D790 |
| Flexural Strength (3.18 mm) | 82.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 17 | kJ/m² | ISO 179/1 |
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.18 mm | 110 | J/m | |
| 23°C, 3.18 mm | 270 | J/m | |
| Gardner Impact (3.18 mm) | 16.9 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 98.9 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 93.3 | °C | |
| RTI Elec | UL 746 | ||
| 3.00 mm | 65.0 | °C | |
| 6.00 mm | 65.0 | °C | |
| RTI Imp | UL 746 | ||
| 3.00 mm | 65.0 | °C | |
| 6.00 mm | 65.0 | °C | |
| RTI Str | UL 746 | ||
| 3.00 mm | 65.0 | °C | |
| 6.00 mm | 65.0 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 3.1E+16 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 3.00 mm, ALL | V-1 | ||
| 6.00 mm, ALL | V-1 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 to 82.2 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 216 to 266 | °C | |
| Middle Temperature | 227 to 271 | °C | |
| Front Temperature | 238 to 277 | °C | |
| Processing (Melt) Temp | 249 to 277 | °C | |
| Mold Temperature | 54.4 to 76.7 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SynPlast™ DINP-N | PolyOne Corporation | Di Isononyl Phthalate | SynPlast™ |
| Tufpet PBT G2810 | Mitsubishi Rayon America Inc. | PBT | Tufpet |
| Ultramid® A3WG7 BK23210 | BASF Corporation | Nylon 66 | Ultramid® |
| Anjacom® 255-GF30 | Almaak International GmbH | Nylon 6 | Anjacom® |
| Gallonprene® GP420-8503 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |