Mecoline I RDX 1229 F
| Category: | TP, Unspecified , Thermoplastic |
| Manufacturer: | Melos GmbH |
| Trademark: | Mecoline |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qlyncP_Mecoline-I-RDX-1229-F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| An e-beam radiation cross-linkable, halogen-free low smoke compound, offering good mechanical and electrical properties. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.37 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (150°C/10.0 kg) | 3.0 | g/10 min | ISO 1133 |
| pH | > 4.7 | IEC 60754-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Hot Set 1 | IEC 540 | ||
| Elongation under load | 20 | % | |
| Residual elongation | 10 | % |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Conductivity | < 2.00 | µS/mm |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Test | < 15.0 | sec | Internal Method |
| Halogen Content | 0 | % | IEC 754-1 |
| Toxicity | < 3.00 | NES 713 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermal Shrinkage - 1hr @ 100°C | < 0.50 | % | Internal Method |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Head Temperature | 170 to 180 | °C | |
| Extruder Screw L/D Ratio | 24.0:1.0 to 26.0:1.0 | ||
| Extruder Screw Compression Ratio | 2.0:1.0 to 3.0:1.0 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 52 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | IEC 811-1-1 | ||
| -- 2 | 15.0 | MPa | |
| -- 3 | > 10.0 | MPa | |
| Tensile Strain | IEC 811-1-1 | ||
| Break 4 | 200 | % | |
| Break 5 | > 230 | % |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 6 | 1.0E+12 | ohms·cm | Internal Method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 27 | % | ASTM D2863 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 120 to 130 | °C | |
| Cylinder Zone 2 Temp. | 130 to 140 | °C | |
| Cylinder Zone 3 Temp. | 130 to 140 | °C | |
| Cylinder Zone 4 Temp. | 140 to 150 | °C | |
| Cylinder Zone 5 Temp. | 150 to 160 | °C | |
| Adapter Temperature | 150 to 160 | °C | |
| Die Temperature | 170 to 180 | °C |
| Note Message | |
|---|---|
| 1 . | at 200°C/15min/0.2 MPa |
| 2 . | After crosslinking |
| 3 . | Before crosslinking |
| 4 . | After crosslinking |
| 5 . | Before crosslinking |
| 6 . | 1h at 70°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 208A MS 5 | RTP Company | Nylon 6 | RTP |
| TECHNYL® A 218 V50 BLACK 21 N | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| Indothene HD 52GB001 | Reliance Industries Limited | HDPE | Indothene HD |
| Lion Idemitsu Composites PPS Y531F1 | Lion Idemitsu Composites Co., Ltd. | PPS | Lion Idemitsu Composites PPS |
| Durez® 34127 | SBHPP | Phenolic | Durez® |