Staramide AK8
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Eurostar Engineering Plastics |
| Trademark: | Staramide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ql9HRn_Staramide-AK8.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Staramide AK8 is a 40 % Mineral Filled Polyamide 66 Injection Molding Resin |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.45 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow 1 | 0.90 to 1.3 | % | Internal Method |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.90 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (L-Scale) | 92 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5200 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 75.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 10 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 5200 | MPa | ISO 178 |
| Flexural Stress | 135 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 3 | ISO 179/1eA | ||
| -30°C | 6.0 | kJ/m² | |
| 23°C | 7.0 | kJ/m² | |
| Charpy Unnotched Impact Strength 4 | ISO 179/1eU | ||
| -30°C | > 100 | kJ/m² | |
| 23°C | > 100 | kJ/m² | |
| Notched Izod Impact Strength 5 | ISO 180/1A | ||
| -30°C | 7.0 | kJ/m² | |
| 23°C | 7.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 6 | |||
| 0.45 MPa, Unannealed, 100 mm Span | 231 | °C | ISO 75-2/Be |
| 1.8 MPa, Unannealed, 100 mm Span | 170 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 252 | °C | ISO 306/B50 |
| -- | 251 | °C | ISO 306/B120 |
| Ball Pressure Test 7(125°C) | Pass | IEC 60695-10-2 | |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 6.0E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 6.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Electric Strength (3.20 mm, in Oil) | 18 | kV/mm | IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | FMVSS 302 | ||
| 2.00 mm | 6.0 | mm/min | |
| 3.00 mm | 2.0 | mm/min | |
| Glow Wire Flammability Index (2.00 mm) | 650 | °C | IEC 60695-2-12 |
| Oxygen Index | 32 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 85.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 260 to 280 | °C | |
| Middle Temperature | 270 to 280 | °C | |
| Front Temperature | 270 to 290 | °C | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 sp=62mm |
| 4 . | 80*10*4 sp=62mm |
| 5 . | 80*10*4 |
| 6 . | 120*10*4 |
| 7 . | 125°C ±2°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sarlink® TPE RV-2235N | Teknor Apex Company | TPE | Sarlink® TPE |
| Tectron E1188 | TECTRON Systems Pte Ltd | TPV | Tectron |
| KumhoSunny PC/ABS HAC8250NH-DF10 | Shanghai KumhoSunny Plastics Co., Ltd. | PC+ABS | KumhoSunny PC/ABS |
| Karina MBPEB WHITE 1000/5035-IE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| HDPE NG 7000 H | The Dow Chemical Company | HDPE | HDPE |