Halene H F5400
| Category: | HDPE, HMW , High Density (HMW) Polyethylene |
| Manufacturer: | Haldia Petrochemicals Ltd. |
| Trademark: | Halene H |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qkFLwk_Halene-H-F5400.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
F5400 is a film grade HM-HDPE manufactured using the Mitsui CX Technology. This can be used for general-purpose Films as well as very thin Reinforced bags. F5400 grade is characterized by excellent processability and high mechanical strength. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 0.954 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.090 | g/10 min | ASTM D1238 |
| 190°C/21.6 kg | 14 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (10% Igepal, Compression Molded, F50) | > 500 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 62 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | ASTM D638 | ||
| Yield, molding | 25.0 | MPa | ASTM D638 |
| Fracture, molding | 38.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, Compression Molded) | 1000 | % | ASTM D638 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dart Drop Impact (20 µm, Blown Film) | 80 | g | ASTM D1709A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, Compression Molded) | 180 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 131 | °C | ASTM D3418 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 180 - 220 | °C | |
| Cylinder Zone 2 Temp. | 180 - 220 | °C | |
| Cylinder Zone 3 Temp. | 180 - 220 | °C | |
| Cylinder Zone 4 Temp. | 180 - 220 | °C | |
| Cylinder Zone 5 Temp. | 180 - 220 | °C |
| Extrusion instructions |
|---|
| BUR: 3 to 6 |
| Note Message | |
|---|---|
| 1 . | 23°C |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SINOF DH-F22E-2 | SINOF HI-TECH MATERIAL CO. LTD | PVDF | SINOF |
| Nypol® PA A3 FR NTLA010 NR309 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| BESTNYL SE10VI02AU | Triesa Plastics | Nylon 66 | BESTNYL |
| Hostacom ERC 2061N | LyondellBasell Industries | PP, Unspecified | Hostacom |
| Sylvin 8380-75 Brown 7438 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |