Hifax CA 207 A is a reactor TPO (thermoplastic polyolefin) manufactured using LyondellBasell`s proprietary Catalloy process technology. It is suitable for injection molding applications as well as for wire & cable extrusion process. As an impact modifier for compounding applications, it can be blended with other polyolefinic resins for a better shrinkage control and to improve the low temperature impact resistance. It does not contain any slip nor anti-blocking agents. The grade is available in natural pellet form. For regulatory compliance information see Hifax CA 207 A Product Stewardship Bulletin (PSB). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.5 | g/10 min | ISO 1133 |
| Molding Shrinkage 1(48 hr, 3.20 mm) | 0.60 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 50 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 14.0 | MPa | |
| Break | 22.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 20 | % | |
| Break | > 800 | % | |
| Flexural Modulus | 500 | MPa | ISO 178 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 2 | 122 | kN/m | ASTM D624 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (-40°C) | 10 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact | ASTM D3763 | ||
| -40°C, Ductile Failure 3 | 23.0 | J | |
| 23°C, Ductile Failure 4 | 16.0 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 60.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 94.0 | °C | ISO 306/A50 |
| Melting Temperature (DSC) | 162 | °C | ISO 3146 |
| Note Message | |
|---|---|
| 1 . | 100x150x3.2 mm |
| 2 . | Die C, 50 mm/min |
| 3 . | 6.60 m/sec |
| 4 . | 2.20 m/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Silopren® LSR 4640FC | Momentive Performance Materials Inc. | Silicone Rubber, LSR | Silopren® |
| BJB Polyurethane WC-753 A/B | BJB Enterprises, Inc. | PUR, Unspecified | BJB Polyurethane |
| Geon™ Vinyl Rigid Molding M3220 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Molding |
| HiFill® PA6 LE BK | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| KOPA® KN333HB640BL | Kolon Plastics, Inc. | Nylon 66 | KOPA® |