TAROLOX 111 G3 DX0
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROLOX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qhq8tg_TAROLOX-111-G3-DX0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TAROLOX 111 G3 DX0 is a Polyethylene Terephthalate (PET) product filled with 15% glass fiber. It can be processed by injection molding and is available in Europe. Typical application: Electrical/Electronic Applications. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.52 to 1.54 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow | 1.0 to 1.2 | % | |
| Flow | 0.30 to 0.50 | % | |
| Water Absorption (23°C, 24 hr) | 0.070 | % | ISO 62 |
| Granule Humidity 1 | < 0.030 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 100 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 1.9 | % | ISO 527-2/50 |
| Flexural Modulus 2 | 9000 | MPa | ISO 178 |
| Flexural Stress 3 | 140 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 40 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ASTM D256 | ||
| -20°C | 50 | J/m | |
| 23°C | 65 | J/m | |
| Notched Izod Impact (Area) (23°C) | 6.00 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4 | |||
| 0.45 MPa, Unannealed | 240 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 200 | °C | ISO 75-2/A |
| Continuous Use Temperature | IEC 60216 | ||
| -- | 140 | °C | |
| -- 5 | 140 | °C | |
| Vicat Softening Temperature | 215 | °C | ISO 306/B50 |
| Ball Pressure Test (245°C) | Pass | IEC 60695-10-2 | |
| Melting Temperature | 256 | °C | ISO 11357-3 |
| CLTE - Flow (-30 to 30°C) | 2.7E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength (1.00 mm) | 34 | kV/mm | IEC 60243-1 |
| Dielectric Constant | 3.10 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 225 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.970 mm | V-0 | ||
| 1.60 mm | V-0 | ||
| 3.20 mm | V-0 | ||
| Glow Wire Flammability Index (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Oxygen Index | 32 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 130 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 260 to 290 | °C | |
| Mold Temperature | 90.0 to 130 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | TARO 002 |
| 2 . | 1.0 mm/min |
| 3 . | 1.0 mm/min |
| 4 . | 120°C/hr |
| 5 . | 20000 hrs |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| STARFLEX® D 2245 | STAR Thermoplastic Alloys & Rubbers, Inc. | TPE | STARFLEX® |
| Braskem PP TR3350MS | Braskem America Inc. | PP Random Copolymer | Braskem PP |
| DAI-EL™ G-723F | Daikin Fluorochemicals (China) Co., Ltd. | Fluorelastomer | DAI-EL™ |
| HiFill® PA6/ABS 1120 B1 | Techmer Engineered Solutions | Nylon 6+ABS | HiFill® |
| Polyrocks EP8400X105V-2 | Polyrocks Chemical Co., Ltd | XLPE | Polyrocks |