MFE® 9503
| Category: | Polyester Alloy , Polyester Alloy |
| Manufacturer: | Huachang Polymer Co., Ltd. |
| Trademark: | MFE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qhN8uA_MFE-9503.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
9503 terephthalic unsaturated polyester resin is researched and manufactured by Huachang Company on the basis of 9709 ORTHO type and 9406 ISO type unsaturated resins, the above-mentioned resins form the series products comprised of terephthalic type, ISO type and ORTHO type. PROPERTY 9503 terephthalic unsaturated polyester resin is charactered by superior thermal resistance, solvent resistance and anticorrosion, inferior solidification shrinkage as well as exceptional mechanical performance. APPLICATION Applied to pultrusion and winding molding process |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Acid Value | 12.00 to 20.00 | mg KOH/g | Internal Method |
| Solids Content | 59 to 65 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermal Stability (80°C) | > 1 | day |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gel Time (25°C) | 10.0 to 18.0 | min | Internal Method |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Cobalt Naphthenate - (promoter) | 1.0 to 4.0 | % | |
| Methyl Ethyl Ketone Peroxide - (curative agent) | 1.0 to 3.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3600 | MPa | Internal Method |
| Tensile Strength | 50.0 | MPa | Internal Method |
| Tensile Elongation (Break) | 2.7 | % | Internal Method |
| Flexural Modulus | 3800 | MPa | Internal Method |
| Flexural Strength | 78.0 | MPa | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 100 | °C | ASTM D648 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Mix Viscosity (25°C) | 350 | cP | Internal Method |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® A CP300K 333 NER | Radici Plastics | Nylon 66 | Radilon® |
| Retpol® PDR 7380/2 UV3 | PolyPacific Pty. Ltd. | PP, Unspecified | Retpol® |
| Ultralloy™ 51-5 | Hapco Inc. | TP, Unspecified | Ultralloy™ |
| Hylon® N2025L | Ravago Manufacturing Americas, LLC | Nylon 6 | Hylon® |
| 3M™ Dyneon™ PTFE Compound TF 7717 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |