Order Products : sales@su-jiao.com
Lushan PJ-1
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Guangzhou Lushan New Materials Co., Ltd |
| Trademark: | Lushan |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qgZ1gl_Lushan-PJ-1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene Compounds for Steel Pipe Top Coats Polypropylene compound for steel pipe top coats Lushan PJ-1 is used for 3LPP coating system in colored white. It is supplied in pellets for melt extrusion or in a powder for application by spray or other special means. Polypropylene compound for steel pipe top coats Lushan PJ-1 was developed by Guangzhou Hot-melt Adhesive Engineering and Technical R&D Center, and used as top coats anti-corrosion material for 3LPP buried anti-corrosion steel pipe coating or coated steel plastic composite pipes in the application of oil& gas transportation systems and high pressure water pipeline system. Polypropylene compound for steel pipe top coats Lushan PJ-1 has good properties such as widely processing range, high compatibility with adhesive and excellent mechanical properties, excellent thermal aging resistance and UV protection, etc. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.906 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.50 | g/10 min | ASTM D1238 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.030 | % | ISO 585 |
| Environmental Stress-Cracking Resistance | 1300 | hr | ISO 21809-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 28.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 500 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 30 | J/m | ASTM D256 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Aging - 100D (140°C) | 23 | % | DIN 30678 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxidation Induction Time (220°C) | 32 | min | ISO 21809-1 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Indentation - Hardness (90°C) | 210.0 | µm | DIN 30678 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -30.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 138 | °C | ASTM D1525 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 25 | kV/mm | IEC 60243-1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecotek® PC40 NL VB02 | Eurotec Engineering Plastics | PC+PBT | Tecotek® |
| TECHNO ABS H530L | Techno Polymer Co, Ltd. | ABS | TECHNO ABS |
| Neopor® 2400 | BASF Corporation | PS (EPS) | Neopor® |
| Karina BLACK PVC COMPOUND -E CAK 65-48/ 1 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Petrothene® M2520 | LyondellBasell Industries | LDPE | Petrothene® |