Description PA66 MOS2 Filled Steel Grey Compound Product Applications This grade is ideal for moving parts Such as Mechanical seal, Bearing slider ring etc Benefits Great Wear resistant, Low surface Friction Higher strength and good rigidity |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.17 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | |||
| Flow | 0.80 | -- | % | ASTM D955 |
| Transverse flow | 0.80 | -- | % | ASTM D955 |
| Water Absorption | ASTM D570 | |||
| 23°C, 24 hr | 0.30 | -- | % | ASTM D570 |
| Saturation 1 | 7.0 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3300 | -- | MPa | ASTM D638 |
| Tensile Strength | 90.0 | 60.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 20 | 25 | % | ASTM D638 |
| Flexural Modulus | 3200 | -- | MPa | ASTM D790 |
| Flexural Strength | 120 | 85.0 | MPa | ASTM D790 |
| Coefficient of Friction | 0.20 | -- | ASTM D1894 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (23°C) | 49 | -- | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, not annealed | 205 | -- | °C | ASTM D648 |
| 1.8 MPa, not annealed | 98.0 | -- | °C | ASTM D648 |
| Melting Temperature | 262 | -- | °C | ASTM D2117 |
| CLTE - Flow (-40 to 149°C) | 7.2E-5 | -- | cm/cm/°C | ASTM E831 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | -- | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 | -- | ohms·cm | IEC 60093 |
| Dielectric Strength | 14 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.800 mm) | V-2 | -- | UL 94 |
| Additional Information |
|---|
| 干燥 This grade is not suitable for food contact, medical devices or toy applications |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Hot Air Dryer | 80.0 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 260 - 270 | °C | |
| Middle Temperature | 270 - 280 | °C | |
| Front Temperature | 270 - 280 | °C | |
| Mold Temperature | 65.0 - 85.0 | °C |
| Note Message | |
|---|---|
| 1 . | Immersed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sarlink® TPE EE-1250N | Teknor Apex Company | TPE | Sarlink® TPE |
| TAIRILOY AC2000 | Formosa Plastics Corporation | PC+ABS | TAIRILOY |
| ADENE NTTAG | A.D. Compound spa | PP Copolymer | ADENE |
| LUBEMID A26 MB NATURAL | LUBEN PLAST srl | Nylon 66 | LUBEMID |
| Hostacom EKC 425N G71412 | LyondellBasell Industries | PP, Unspecified | Hostacom |