Toyolac® 950-X01
| Category: | MABS , Methyl Methacrylate / ABS |
| Manufacturer: | Toray Resin Company |
| Trademark: | Toyolac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qexLLN_Toyolac-950-X01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Toyolac® 950-X01 is a Methyl Methacrylate / ABS (MABS) product. It is available in Asia Pacific, Europe, or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Part Marking Code |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.09 | g/cm³ | ASTM D792 |
| 23°C | 1.09 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 18 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.40 to 0.60 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 110 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- | 43.0 | MPa | ASTM D638 |
| 23°C | 50.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 20 | % | ASTM D638 |
| Break, 23°C | 14 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2100 | MPa | ASTM D790 |
| 23°C | 2180 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 67.0 | MPa | ASTM D790 |
| 23°C | 71.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 14 | kJ/m² | ISO 179 |
| Notched Izod Impact | ASTM D256 | ||
| 23°C, 3.20 mm | 180 | J/m | |
| 23°C, 12.7 mm | 170 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 6.40 mm | 79.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 75.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 80.0 to 85.0 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (Total, 3000 µm) | 86.0 | % | ISO 13468 |
| Haze (3000 µm) | 3.0 | % | ISO 14782 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Thermoplastic Polyolefin FT1055-624 | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| Resirene 6470 | Resirene, S.A. de C.V. | PS (HIPS) | Resirene |
| Gallonprene® GP210-4002L | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Karina IVORY PVC COMPOUND -E 105902-35/ 1-Y-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 8355-65 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |