Adiprene® LFP 1950A
| Category: | PUR-Ester/PPDI , Polyurethane (Polyester, PPDI) |
| Manufacturer: | Chemtura |
| Trademark: | Adiprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qeuKpu_Adiprene-LFP-1950A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ADIPRENE LFP 1950A is a PPDI-terminated polyester prepolymer having very low free PPDI content (typical < 0.1%) for easier management of health and safety during handling. This prepolymer is similar to ADIPRENE PP 1095H in composition and performance, while offering significant processing advantages including easier melting, lower viscosity, and increased pour life. ADIPRENE LFP 1950A yields a high performance 93-95 Shore A hardness elastomer when cured with VIBRACURE® A 250. The high performance features of ADIPRENE LFP 1950A are due to PPDI (p-phenylene diisocyanate), a special building block that imparts exceptional properties to cast polyurethane elastomers. The unique combination of properties exhibited by PPDI-based prepolymers is superior to those available from standard prepolymers based on TDI or MDI. Features of ADIPRENE LFP 1950A include:
|
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 93 to 95 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Compressive Strength | ASTM D695 | ||
| 5% Strain | 2.48 | MPa | |
| 10% Strain | 4.83 | MPa | |
| 15% Strain | 6.89 | MPa | |
| 20% Strain | 9.31 | MPa | |
| 25% Strain | 12.1 | MPa |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% Strain | 9.65 | MPa | |
| 300% Strain | 13.8 | MPa | |
| Tensile Strength | 48.3 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 650 | % | ASTM D412 |
| Tear Strength (Split) | 28 | kN/m | ASTM D470 |
| Compression Set | ASTM D395B | ||
| 70°C, 22 hr | 35 | % | |
| 100°C, 22 hr | 50 | % | |
| Bayshore Resilience | 57 | % | ASTM D2632 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Pot Life | 6.0 | min | |
| Demold Time | > 60 | min | |
| Post Cure Time (116°C) | 16 | hr |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Dynamic Properties | |||
| Storage Modulus : 30°C | 3.14E+8 | dynes/cm² | |
| Storage Modulus : 150°C | 2.42E+8 | dynes/cm² | |
| Tangent Delta : 30°C | 0.0180 | ||
| Tangent Delta : 150°C | 0.0140 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 6 MKF 4015 K2098 | A. Schulman Europe | Nylon 6 | SCHULAMID® |
| DJSilicone NE-270 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| Firepel® K130-LCS-00 | AOC, L.L.C. | Polyester Alloy | Firepel® |
| PLANAC BT-2230-60 | TOYOBO America, Inc. | PBT | PLANAC |
| Rotuba CAP CP800 (13% Plasticizer) | Rotuba Extruders, Inc. | CAP | Rotuba CAP |