DOW™ LDPE 611A
| Category: | LDPE , Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOW™ LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qeZgCF_DOW-LDPE-611A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
| General Information | |
|---|---|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.924 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.88 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film strength | ASTM D882 | ||
| MD : 25 µm | 55.1 | J/cm³ | ASTM D882 |
| MD : 51 µm | 64.5 | J/cm³ | ASTM D882 |
| TD : 25 µm | 63.7 | J/cm³ | ASTM D882 |
| TD : 51 µm | 66.9 | J/cm³ | ASTM D882 |
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 25 µm | 197 | MPa | ASTM D882 |
| 2% secant, MD : 51 µm | 201 | MPa | ASTM D882 |
| 2% secant, TD : 25 µm | 225 | MPa | ASTM D882 |
| 2% secant, TD : 51 µm | 227 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 25 µm | 11.9 | MPa | ASTM D882 |
| MD : Yield, 51 µm | 11.8 | MPa | ASTM D882 |
| TD : Yield, 25 µm | 12.3 | MPa | ASTM D882 |
| TD : Yield, 51 µm | 12.2 | MPa | ASTM D882 |
| MD : Break, 25 µm | 25.4 | MPa | ASTM D882 |
| MD : Fracture, 51 µm | 21.6 | MPa | ASTM D882 |
| TD : Break, 25 µm | 17.3 | MPa | ASTM D882 |
| TD : Fracture, 51 µm | 16.9 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 25 µm | 270 | % | ASTM D882 |
| MD : Fracture, 51 µm | 370 | % | ASTM D882 |
| TD : Break, 25 µm | 540 | % | ASTM D882 |
| TD : Fracture, 51 µm | 560 | % | ASTM D882 |
| Dart Drop Impact | ASTM D1709A | ||
| 25 µm | 78 | g | ASTM D1709A |
| 51 µm | 120 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm | 190 | g | ASTM D1922 |
| MD : 51 µm | 400 | g | ASTM D1922 |
| TD : 25 µm | 180 | g | ASTM D1922 |
| TD : 51 µm | 450 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 97.2 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 112 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | ASTM D2457 | ||
| 45°, 25.4 µm | 71 | ASTM D2457 | |
| 45°, 50.8 µm | 76 | ASTM D2457 | |
| Haze | ASTM D1003 | ||
| 25.4 µm | 6.0 | % | ASTM D1003 |
| 50.8 µm | 7.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 213 | °C |
| Extrusion instructions |
|---|
| 吹塑薄膜的制造条件： 螺杆类型：单跨 模具间隙：40 密尔 (1.02 mm) 熔体温度：416°F (213°C) 输出：模具周长的 10 磅/小时/英寸 模具直径：6 英寸 放大比：2.5:1 螺杆速度：130 rpm 冷冻线高度：28 英寸 (711 mm) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| URE-BOND® II | Smooth-On, Inc | PUR, Unspecified | URE-BOND® |
| Norpex® PPE AX265 | Custom Resins Group | PPE | Norpex® |
| Hanwha Total PP FB71 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| MAJORIS ET 450 | AD majoris | PP, Unspecified | MAJORIS |
| Sylvin 8355-65 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |