Plenco 06401 (Compression)
| Category: | Phenolic , Phenolic |
| Manufacturer: | Plastics Engineering Co. |
| Trademark: | Plenco |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qbu3ES_Plenco-06401-Compression-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PLENCO 06401 is a glass fiber and mineral filled two-stage phenolic molding compound. UL recognized under component file E40654. 06401 is available in black. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.75 | g/cm³ | ASTM D792 |
| Apparent Density | 0.74 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow | 0.15 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.070 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (E-Scale) | 97 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 14600 | MPa | ASTM D638 |
| Tensile Strength | 69.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 0.60 | % | ASTM D638 |
| Flexural Modulus | 13100 | MPa | ASTM D790 |
| Flexural Strength | 119 | MPa | ASTM D790 |
| Compressive Strength | 253 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 39.6 | J/m | ASTM D256 |
| Notched Izod Impact | 39 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 227 | °C | ASTM D648 |
| Continuous Use Temperature | 226 | °C | ASTM D794 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 3.4E+12 | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 15 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 5.20 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.025 | ASTM D150 | |
| Arc Resistance | 96.0 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 175 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Additional Information |
|---|
| The value listed as Comparative Tracking Index, UL 746 was tested according to ASTM D3638.The value listed as Mold Shrink, Linear-Flow, ASTM D955 was tested according to the ASTM D6289 standard.Post Shrinkage, ASTM D6289, 72hr, 120°C: 0.05%Drop Ball Impact, PLENCO Method: 275 J/m |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 165 - 182 | °C | |
| Back Pressure | 0.300 | MPa | |
| Screw Speed | < 60 | rpm |
| Injection instructions |
|---|
| Mold Close Time: 3-8 sec |
| Note Message | |
|---|---|
| 1 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X4055 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Scolefin 53 G 13-0 | Ravago Group | PP Homopolymer | Scolefin |
| NuSil CV3-2640 | NuSil Technology | Silicone | NuSil |
| Anjacom® J350-GF30 | Almaak International GmbH | Nylon 66 | Anjacom® |
| Globalprene® 9901 | Lee Chang Yung Chemical Industry Corp. | SEBS | Globalprene® |