EPLAMID 66 GV0 30 NC
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | EPSAN Plastik SAN. ve TiC. A.S. |
| Trademark: | EPLAMID 66 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qaodLq_EPLAMID-66-GV0-30-NC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Flame retardant polyamide 66 reinforced with 30% of glass fiber, heat stabilized for injection moulding. Halogenated flame retardant grade, compliance with RoHs derivatives, with rating UL94 V0 and glow-wire at 960°C, combines excellent all around mechanical properties. This product is available in natural and in colours on request. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.60 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction : 3.00mm | 0.60 | -- | % | ISO 294-4 |
| Flow direction : 3.00mm | 0.40 | -- | % | ISO 294-4 |
| Moisture Content | 0.20 | -- | % | ISO 15512 |
| Ash Content | 30 | -- | % | ISO 3451-4 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Durometer Hardness (Shore D, 23°C) | 87 | -- | ISO 868 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 10000 | 9400 | MPa | ISO 527-2/50 |
| Tensile Stress (Break, 23°C) | 160 | 145 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | 2.0 | 4.0 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 9500 | 9200 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 250 | 230 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | 12 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 9.0 | 10 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature 3 | ||||
| 0.45 MPa, not annealed | 250 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 245 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 250 | -- | °C | ISO 306/B120 |
| Melting Temperature (DSC) | 255 | -- | °C | ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index (Solution A) | 400 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | -- | UL 94, IEC 60695-11-10, -20 | |
| Glow Wire Flammability Index (0.800 mm) | 960 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (0.800 mm) | 750 | -- | °C | IEC 60695-2-13 |
| Additional Information |
|---|
| 干燥 TEST CONDITIONS: Laboratory conditions are 23 ±2°C and 45-55 % RH. |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Processing (Melt) Temp | 280 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 120°C/h |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRISTAR® PC-10FRN(V) | Polymer Technology and Services, LLC | PC | TRISTAR® |
| Badaprene® TPV 70A 1079 | Bada AG | PP+EPDM | Badaprene® |
| Iupiace® GX1050 | Mitsubishi Engineering-Plastics Corp | PPE+PS | Iupiace® |
| Purell RP170G | LyondellBasell Industries | PP, Unspecified | Purell |
| TOTAL Polyethylene HDPE SB 1359 NA | TOTAL Refining & Chemicals | HDPE | TOTAL Polyethylene |