Lucel® N109WR
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lucel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qaHTmX_Lucel-N109WR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lucel®N109WR is a polyoxymethylene (POM) copolymer material,. This product is available in North America, Latin America, Europe or Asia Pacific. The processing method is injection molding. Lucel®The main features of N109WR are:
Lucel®Typical application areas of N109WR are: automotive industry |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 9.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 1.8 - 2.1 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 82 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 60.8 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 65 | % | ASTM D638 |
| Flexural Modulus 3(6.40 mm) | 2550 | MPa | ASTM D790 |
| Flexural Strength 4(6.40 mm) | 89.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.40 mm) | 69 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, annealed, 6.40mm | 160 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 110 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257 |
| Volume Resistivity (23°C) | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C, 1.00 mm) | 24 | kV/mm | ASTM D149 |
| Dissipation Factor (1 MHz) | 3.8E-4 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.710 mm | HB | UL 94 | |
| 1.50 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 - 110 | °C | |
| Drying Time | 3.0 - 6.0 | hr | |
| Rear Temperature | 160 - 180 | °C | |
| Middle Temperature | 180 - 200 | °C | |
| Front Temperature | 190 - 200 | °C | |
| Nozzle Temperature | 190 - 200 | °C | |
| Processing (Melt) Temp | 190 - 200 | °C | |
| Mold Temperature | 60.0 - 80.0 | °C | |
| Back Pressure | 4.02 - 8.04 | MPa | |
| Screw Speed | 50 - 100 | rpm |
| Injection instructions |
|---|
| Minimum Moisture Content: 0.1% |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Miramid® S3C | BASF Leuna GmbH | Nylon 66 | Miramid® |
| RTP 101 CC UV | RTP Company | PP, Unspecified | RTP |
| Bormod™ HD905CF | Borealis AG | PP Homopolymer | Bormod™ |
| ALPERFORM PC LD | ALBIS PLASTIC GmbH | PC | ALPERFORM |
| Sylvin 5132-86 Clear Green 3166 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |