LNP™ STAT-KON™ DE0029 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qXT1t3_LNP-STAT-KON-DE0029-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON DE0029 is a compound based on Polycarbonate resin containing 10% Carbon Fiber. Added features of this material include: Electrically Conductive, Flame Retardant. Also known as: LNP* STAT-KON* Compound DC-1002 FR Product reorder name: DE0029 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.29 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.10 to 0.30 | % | ASTM D955 |
| Across Flow : 24 hr | 0.30 to 0.50 | % | ASTM D955 |
| Across Flow : 24 hr | 0.39 | % | ISO 294-4 |
| Flow : 24 hr | 0.19 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Break | 105 | MPa | ASTM D638 |
| Break | 104 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 5.9 | % | ASTM D638 |
| Break | 6.2 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 7580 | MPa | ASTM D790 |
| -- | 7400 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 159 | MPa | ASTM D790 |
| -- | 149 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 59 | J/m | ASTM D256 |
| 23°C 1 | 5.3 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 490 | J/m | ASTM D4812 |
| 23°C 2 | 32 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 294 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 3 | 145 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 286 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 142 | °C | ISO 75-2/Af |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+3 to 1.0E+6 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+4 to 1.0E+7 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 80*10*4 |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 mm |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premier PR350M | Premier Polymers, LLC. | PP Random Copolymer | Premier |
| RX® 655 | Sumitomo Bakelite North America, Inc. | Phenolic | RX® |
| THERMOLAST® K TC4PAZ (Series: AD/PA) | KRAIBURG TPE | TPE | THERMOLAST® K |
| MAJORIS EE165 - 1791 | AD majoris | PP, Unspecified | MAJORIS |
| Sylvin 6185-80 Red 6204 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |