DOW™ LDPE 582E
| Category: | LDPE , Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOW™ LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qXIPZQ_DOW-LDPE-582E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DOW LDPETM 582E polyethylene resin can be extruded by ordinary blown film process, and the melt temperature is between 150 and 170°C. At the time of preparation, DOW LDPE 582E polyethylene resin had good mechanical properties and high optical properties. The product has good drafting performance and excellent processing performance. This product contains slip agent and opening agent. regulatory requirements: DOW LDPE 582E polyethylene resin shall meet the following regulatory requirements: U.S. food and drug administration regulation 21 CFR 177.1520(c) 2.2 EU, No 10/2011 U.S. FDA-DMF please consult the regulations for complete details. Application field:
|
| General Information | |
|---|---|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.923 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.5 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | 0.16 - 0.20 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 50 µm | 190 | MPa | ASTM D882 |
| 2% secant, TD : 50 µm | 175 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 50 µm | 9.00 | MPa | ASTM D882 |
| TD : Yield, 50 µm | 9.00 | MPa | ASTM D882 |
| MD : Break, 50 µm | 17.0 | MPa | ASTM D882 |
| TD : Break, 50 µm | 15.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 50 µm | 450 | % | ASTM D882 |
| TD : Break, 50 µm | 650 | % | ASTM D882 |
| Dart Drop Impact (50 µm) | 120 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 50 µm | 500 | g | ASTM D1922 |
| TD : 50 µm | 400 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 93.0 | °C | ISO 306/A |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (20°, 50.0 µm) | 70 | ASTM D2457 | |
| Haze (50.0 µm) | 7.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 150 - 170 | °C |
| Extrusion instructions |
|---|
| 放大比 1:2.5 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Baydur® 665 IBS (25 pcf) | Covestro - PUR | PUR-MDI | Baydur® |
| Alpha PVC GW 3040-LT NATURAL LCF | AlphaGary | PVC, Unspecified | Alpha PVC |
| KPOL-NYLON K-NY66/21VO | KPOL Chem Co. | Nylon 66 | KPOL-NYLON |
| Hostacom TRC 787N E G82787 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Sylvin 9077-95 Yellow 4185 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |