Chemlon® 140 BH
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Teknor Apex Company (Chem Polymer) |
| Trademark: | Chemlon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qWMGwU_Chemlon-140-BH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Chemlon® 140 BH is a Polyamide 66 (Nylon 66) material filled with glass bead. It is available in Asia Pacific, Europe, or North America for injection molding. Primary attribute of Chemlon® 140 BH: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.44 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow 1 | 1.0 to 1.5 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.90 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 86.2 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 3.0 | % | |
| Break | 4.0 | % | |
| Flexural Modulus | 4720 | MPa | ASTM D790 |
| Flexural Strength | 134 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 43 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 242 | °C | |
| 1.8 MPa, Unannealed | 215 | °C | |
| Melting Temperature | 257 | °C | ASTM D789 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength (3.00 mm) | 15 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 2(0.810 mm) | HB | UL 94 | |
| Oxygen Index | 27 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 241 to 257 | °C | |
| Middle Temperature | 257 to 271 | °C | |
| Front Temperature | 263 to 279 | °C | |
| Nozzle Temperature | 263 to 282 | °C | |
| Processing (Melt) Temp | 263 to 282 | °C |
| Note Message | |
|---|---|
| 1 . | Dependent upon molding conditions particularly Mold temperature. |
| 2 . | Chem Polymer measurement according to UL. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sarlink® TPV X17175B | Teknor Apex Company | TPV | Sarlink® TPV |
| CEPLA CW-452E | CEPLA Co., LTD | PP, Unspecified | CEPLA |
| Chemraz 661 | Greene, Tweed & Co. | Perfluoroelastomer | Chemraz |
| Durez® 153 (Injection) | Sumitomo Bakelite North America, Inc. | Phenolic | Durez® |
| KOPLA PA66 KDG1080 | KOPLA Co., Ltd. | Nylon 66 | KOPLA PA66 |