SCHULAMID® 612 FS 5003 MC
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qU8dSf_SCHULAMID-612-FS-5003-MC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High impact modified Polyamide 612 with heat stabilization |
| General Information | |
|---|---|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.04 | -- | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (245°C/5.0 kg) | 15.0 | -- | cm³/10min | ISO 1133 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 1900 | 830 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 50.0 | 35.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 5.5 | 22 | % | ISO 527-2/1A/50 |
| Nominal Tensile Strain at Break | 35 | 300 | % | ISO 527-2/1A/50 |
| Flexural Modulus 1 | 1500 | -- | MPa | ISO 178 |
| Flexural Stress 2 | ISO 178 | |||
| 3.5% Strain | 48.0 | -- | MPa | |
| 7.1% Strain | 61.0 | -- | MPa |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | 22 | -- | kJ/m² | |
| -30°C | 25 | -- | kJ/m² | |
| 23°C | 75 | 120 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -40°C | No Break | -- | ||
| -30°C | No Break | -- | ||
| 23°C | No Break | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 108 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 90.0 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | ||||
| -- | 205 | -- | °C | ISO 306/A50 |
| -- | 146 | -- | °C | ISO 306/B50 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate (2.00 mm) | 20 | -- | mm/min | ISO 3795 |
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 1.50 mm | 675 | -- | °C | |
| 3.00 mm | 675 | -- | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 1.50 mm | 700 | -- | °C | |
| 3.00 mm | 700 | -- | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 209 K TFE 15 | RTP Company | PARA | RTP |
| Prime Polypro™ J-750HP | Prime Polymer Co., Ltd. | PP Copolymer | Prime Polypro™ |
| Ecomass® 1080ZG90 | Ecomass Technologies | Nylon 12 | Ecomass® |
| EdgeGlas® TP | Plastic Selection Group, Inc. | TP, Unspecified | EdgeGlas® |
| LNP™ THERMOCOMP™ BF004 compound | SABIC Innovative Plastics | SAN | LNP™ THERMOCOMP™ |