Arlon® 35NQ
| Category: | PI, TP , Thermoplastic Polyimide |
| Manufacturer: | Arlon-MED |
| Trademark: | Arlon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qTCZrl_Arlon-35NQ.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 35NQ is a pure polyimide laminate and prepreg system. Reinforced with woven Quartz fabric, combining the advantages of a reduced cure cycle, high temperature polyimide system (Tg >/=250°C), with low dielectric constant and loss tangent (DK = 3.5, loss 0.009 at 1 MHz) for applications requiring operation at RF/Microwave frequencies. Polyimide Quartz materials also exhibit reduced in-plane CTE for expansion matched SMT applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Water Absorption (24 hr) | 0.25 | % | Internal Method |
| Decomposition Temperature | Internal Method | ||
| 5% | 407 | °C | |
| Intial | 363 | °C |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peel Strength | Internal Method | ||
| -- 1 | 1.1 | kN/m | |
| -- 2 | > 1.1 | kN/m | |
| -- 3 | 1.1 | kN/m |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Expansion Rate (50 to 260°C) 4 | 1.1 | % | Internal Method |
| T260 | > 1.0 | hr | Internal Method |
| T288 | > 1.0 | hr | Internal Method |
| T300 | 11.0 | min | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 20700 | MPa | Internal Method |
| Flexural Strength | 655 | MPa | Internal Method |
| Poisson's Ratio 5 | 0.15 | ASTM D3039 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | > 250 | °C | Internal Method |
| CLTE - Flow | |||
| -- 6 | 9.0E-6 to 1.0E-5 | cm/cm/°C | Internal Method |
| < 250°C 7 | 5.0E-5 | cm/cm/°C | Internal Method |
| > 250°C 8 | 1.5E-4 | cm/cm/°C | Internal Method |
| Thermal Conductivity (100°C) | 0.20 | W/m/K | ASTM E1461 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 9 | 8.0E+15 | ohms | Internal Method |
| Volume Resistivity 10 | 5.0E+15 | ohms·cm | Internal Method |
| Dielectric Strength | 40 | kV/mm | Internal Method |
| Dielectric Constant (1 MHz) | 3.50 | Internal Method | |
| Dissipation Factor (1 MHz) | 9.0E-3 | Internal Method | |
| Arc Resistance | 165 | sec | Internal Method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-1 | UL 94 |
| Note Message | |
|---|---|
| 1 . | After Thermal Stress |
| 2 . | At Elevated Temperatures |
| 3 . | After Process Solutions |
| 4 . | Z-Axis |
| 5 . | x and y direction |
| 6 . | Y-axis |
| 7 . | Z-axis |
| 8 . | Z-axis |
| 9 . | C96/35/90 |
| 10 . | C96/35/90 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SILVER® PC2540.HF | Guangdong Silver Age Sci & Tech. Co., Ltd | PC+ABS | SILVER® |
| Synres® SR-1209A | Teknor Apex Company | PP, Unspecified | Synres® |
| EL-Lene™ H5480S | SCG Chemicals Co., Ltd. | HDPE | EL-Lene™ |
| LNP™ LUBRICOMP™ RX06480 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |
| LEXAN™ HFD4412 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |