DuPure® SL 50
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Ducor Petrochemicals BV |
| Trademark: | DuPure® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qT6TkQ_DuPure-SL-50.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description DuPure SL 50 is a heterophasic polypropylene copolymer. Applications DuPure SL 50 is suitable for: general injection moulding applications, e.g. houseware, closures, cylindrical containers, and furniture. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.910 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.0 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 132/30) | 53.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1250 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 26.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 8.0 | % | |
| Break | > 50 | % | |
| Tensile Creep Modulus 1(1000 hr) | 260 | MPa | ISO 899-1 |
| Shear Modulus | 620 | MPa | ISO 6721-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 2.5 | kJ/m² | |
| -20°C | 3.0 | kJ/m² | |
| 0°C | 4.0 | kJ/m² | |
| 23°C | 7.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 95 | kJ/m² | |
| -20°C | 110 | kJ/m² | |
| 0°C | 160 | kJ/m² | |
| 23°C | No Break | ||
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | 2.5 | kJ/m² | |
| -20°C | 3.0 | kJ/m² | |
| 0°C | 4.0 | kJ/m² | |
| 23°C | 7.5 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 77.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 54.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 151 | °C | ISO 306/A |
| -- | 66.0 | °C | ISO 306/B |
| Melting Temperature (DSC) | 163 | °C | ISO 3146 |
| Note Message | |
|---|---|
| 1 . | elongation <0.5% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SNOLEN® EB 1.5/56 | JSC Gazprom neftekhim Salavat | HDPE | SNOLEN® |
| Zhongfa PBT G-10V | Yuyao Zhongfa Engineering Plastics Co. Ltd. | PBT | Zhongfa |
| 3M™ Dyneon™ Fluoroplastic PFA 6515TZ | 3M Advanced Materials Division | PFA | 3M™ Dyneon™ Fluoroplastic |
| EcoBlend® PAE9730 | Shanghai KumhoSunny Plastics Co., Ltd. | ABS+PET | EcoBlend® |
| Plaslube® J-1300/30/TF/15 | Techmer Engineered Solutions | PPS | Plaslube® |