SINOF DH-F22M
| Category: | PVDF , Polyvinylidene Fluoride |
| Manufacturer: | SINOF HI-TECH MATERIAL CO. LTD |
| Trademark: | SINOF |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qRvzEr_SINOF-DH-F22M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| DH-F22M is a kind of pellet PVDF; has high melting viscosity and suitable for making various PVDF products through compression molding. Products made from DH-F22M have a wide range of service temperature (-50°C to 150°C). |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.75 to 1.79 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/5.0 kg) | 1.0 to 5.0 | g/10 min | ASTM D1238 |
| Water Absorption (Equilibrium) | < 0.050 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 76 to 80 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | ASTM D638 | ||
| Yield, 23°C | > 35.0 | MPa | |
| 23°C | > 30.0 | MPa | |
| Tensile Elongation 3(Break, 23°C) | > 25 | % | ASTM D638 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature 4 | 165 to 171 | °C | ASTM D3418 |
| Note Message | |
|---|---|
| 1 . | 23°C |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrant EPP Proteus® Black | Quadrant Engineering Plastic Products | PP Homopolymer | Quadrant EPP |
| ResMart Plus ABS Black | ResMart | ABS | ResMart Plus |
| Next Nylon 6 Prime Series NGM40-01BK | Next Polymers Ltd. | Nylon 6 | Next Nylon 6 Prime Series |
| GLAMIDE® T-422VOR | TOYOBO America, Inc. | Nylon 6 | GLAMIDE® |
| Keliren® CM3615 | Hangzhou Keli Chemical Co., Ltd. | CPE | Keliren® |