HiFill® PPA GF35 HS LAHW BK MB
| Category: | PPA , Polyphthalamide |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | HiFill® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qRYiY2_HiFill-PPA-GF35-HS-LAHW-BK-MB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High Temperature Nylon |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.45 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 1.0 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.29 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 172 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.3 | % | ASTM D638 |
| Flexural Modulus | 11200 | MPa | ASTM D790 |
| Flexural Strength | 241 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 75 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 300 | °C | ASTM D648 |
| CLTE - Flow | 7.2E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 20 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 327 to 360 | °C | |
| Middle Temperature | 327 to 360 | °C | |
| Front Temperature | 327 to 360 | °C | |
| Processing (Melt) Temp | 316 to 338 | °C | |
| Mold Temperature | 93.3 to 149 | °C | |
| Back Pressure | 0.00 to 0.345 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Scolefin 42 G 25-9 | Ravago Group | PP Copolymer | Scolefin |
| UBE Nylon 5021 T | UBE Engineering Plastics, S.A. | Nylon 66/6 | UBE Nylon |
| BMC 1100 CoreLyn | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| FHR EPS 71-7371 | Flint Hills Resources, LP | PS (EPS) | FHR EPS |
| Sylvin 8200-60UV Clear 876 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |