Elastollan® 1195 A 10 FC
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | BASF Polyurethanes GmbH |
| Trademark: | Elastollan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qR0XvO_Elastollan1195A10FC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Thermoplastic Polyether-Polyurethane with outstanding hydrolysis resistance, low temperature flexibility and high resistance to micro-organisms. General suitability for food contact related applications in FDA and EU regulated markets (please see food contact information). |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.15 | g/cm³ | ISO 1183/A |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ISO 7619 | ||
| Shao A, 3 seconds | 96 | ISO 7619 | |
| Shaw D, 3 seconds | 48 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion Loss | 25.0 | mm³ | ISO 4649-A |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | DIN 53504-S2 | ||
| 20% strain | 6.00 | MPa | DIN 53504-S2 |
| 100% strain | 10.0 | MPa | DIN 53504-S2 |
| 300% strain | 18.0 | MPa | DIN 53504-S2 |
| Tensile Stress | DIN 53504-S2 | ||
| Yield | 55.0 | MPa | DIN 53504-S2 |
| Yield 1 | 37.0 | MPa | DIN 53504-S2 |
| Tensile Elongation (Break) | 500 | % | DIN 53504-S2 |
| Tear Strength 2 | 100 | kN/m | ISO 34-1 |
| Compression Set (23°C, 72 hr) | 30 | % | ISO 815 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | No Break | ISO 179 | |
| 23°C | No Break | ISO 179 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90 - 110 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 40 | °C | |
| Rear Temperature | 190 - 210 | °C | |
| Middle Temperature | 200 - 220 | °C | |
| Front Temperature | 210 - 230 | °C | |
| Nozzle Temperature | 210 - 230 | °C | |
| Processing (Melt) Temp | 210 - 230 | °C | |
| Mold Temperature | 15 - 70 | °C | |
| Injection Rate | Slow | ||
| Back Pressure | 5.00 - 15.0 | MPa |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 150 - 170 | °C | |
| Cylinder Zone 2 Temp. | 160 - 180 | °C | |
| Cylinder Zone 3 Temp. | 170 - 190 | °C | |
| Cylinder Zone 4 Temp. | 190 - 210 | °C | |
| Adapter Temperature | 195 - 215 | °C | |
| Die Temperature | 185 - 205 | °C |
| Note Message | |
|---|---|
| 1 . | After storage in water at 80°C for 42 days |
| 2 . | Method B, right-angle specimen (cut) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| STABAMID® 27 AE 1 | Solvay Polyamide & Intermediates | Nylon 66 | STABAMID® |
| FLEXCHEM™ 4051-02 | Colorite Polymers | PVC, Flexible | FLEXCHEM™ |
| Geon™ Vinyl Flexible XV3870 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| KumhoSunny PC 2502NH | Shanghai KumhoSunny Plastics Co., Ltd. | PC | KumhoSunny PC |
| LEXAN™ EXL1182T resin | SABIC Innovative Plastics | PC | LEXAN™ |