TEKAMID™ TA210HI
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Mando Advanced Materials Co., Ltd. |
| Trademark: | TEKAMID™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qQrMgG_TEKAMID-TA210HI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TEKAMID™ TA210HI is a Polyamide 66 (Nylon 66) product. It is available in Asia Pacific. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.11 | g/cm³ | ASTM D792 |
| Molding Shrinkage 1 | ASTM D955 | ||
| Flow | 1.5 | % | |
| Across Flow | 1.5 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 65.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 60 | % | ASTM D638 |
| Flexural Modulus | 2260 | MPa | ASTM D790 |
| Flexural Strength | 93.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 160 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 225 | °C | |
| 1.8 MPa, Unannealed | 75.0 | °C | |
| Peak Melting Temperature | 260 | °C | ASTM D2133 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | 60°C Mold Temperature |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1200.5-90A | RTP Company | TPU-Polyester | RTP |
| Strator® C-6 HTX | EPIC Polymers | Nylon 66/6 | Strator® |
| Chemlon® 206 GH | Teknor Apex Company (Chem Polymer) | Nylon 6 | Chemlon® |
| Evateno® HM-150 | Braskem | EVA | Evateno® |
| MAJORIS DW434E/8 | AD majoris | HDPE | MAJORIS |