VENYL SW502H - 8229
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | AD majoris |
| Trademark: | VENYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qQDqeH_VENYL-SW502H---8229.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VENYL SW502H - 8229 is a 50% glass fiber filled polyamide 6 medium viscosity intended for Injection moulding. APPLICATIONS VENYL SW502H - 8229 has been developed especially for very demanding applications in automotive industry and electrical parts. VENYL SW502H - 8229 is available in both black and natural (VENYL SW502H) but other colours can be provided on request. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.56 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.20 to 0.40 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.5 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 15500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 185 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2 |
| Flexural Modulus | 12500 | MPa | ISO 178 |
| Flexural Stress | 285 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 18 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 75 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 220 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 212 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 220 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | DIN 53482 |
| Volume Resistivity | 1.0E+14 | ohms·cm | DIN 53482 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 265 to 280 | °C | |
| Middle Temperature | 255 to 270 | °C | |
| Front Temperature | 255 to 270 | °C | |
| Nozzle Temperature | 240 to 275 | °C | |
| Mold Temperature | 60.0 to 100 | °C | |
| Injection Pressure | 60.0 to 90.0 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 50.0 to 70.0 | MPa | |
| Screw L/D Ratio | 15.0:1.0 to 20.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reblend® SC5515UA NAT | SO.F.TER. SPA | PC+ABS | Reblend® |
| TOTAL Polypropylene PPH 3962 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| Complet® LBF40-PA66 | PlastiComp, Inc. | Nylon 66 | Complet® |
| Plaskon SMT-B-2FP | Cookson Electronics - Semiconductor Products | Epoxy | Plaskon |
| SABIC® PPcompound 7175U | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |