EnCom GPTF30 PPE-PA
| Category: | Nylon+PPE , Polyamide + PPE |
| Manufacturer: | EnCom, Inc. |
| Trademark: | EnCom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qMAxhS_EnCom-GPTF30-PPE-PA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% Glass+PTFE Filled PPE/PA Alloy |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.39 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.30 to 0.50 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 146 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 6.0 | % | ASTM D638 |
| Flexural Modulus | 8100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 85 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 252 | °C | |
| 1.8 MPa, Unannealed | 239 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 to 107 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Drying Time, Maximum | 7.0 | hr | |
| Suggested Max Moisture | 5.0E-4 | % | |
| Suggested Shot Size | 40 to 75 | % | |
| Rear Temperature | 260 to 299 | °C | |
| Middle Temperature | 266 to 299 | °C | |
| Front Temperature | 271 to 299 | °C | |
| Nozzle Temperature | 277 to 299 | °C | |
| Processing (Melt) Temp | 277 to 299 | °C | |
| Mold Temperature | 65.6 to 121 | °C | |
| Back Pressure | 0.172 to 0.689 | MPa | |
| Screw Speed | 20 to 100 | rpm | |
| Vent Depth | 0.038 to 0.076 | mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PrimoPrene 65A-4000 | KMI Group Inc. | TPV Alloy | PrimoPrene |
| RheTech Polypropylene HP514-197 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| Staramide RF008U | Eurostar Engineering Plastics | Nylon 66/6 | Staramide |
| Moplen HP553R | LyondellBasell Industries | PP Homopolymer | Moplen |
| DuraElast 1730-60 | Evermore Chemical Industry Co., Ltd. | TPU-Polyester | DuraElast |