P84® Fibers

Category:	API , Aromatic Polyimide
Manufacturer:	Evonik Industries AG
Trademark:	P84®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	qLooVa_P84-Fibers.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
P84® polyimide derived from aromatic dianhydrides and aromatic diisocyanates exhibits outstanding thermal stability. The polymer is non melting, has a glass transition temperature of 315°C. The fibres start to carbonize at temperatures beyond 370 °C. Due to the aromatic structure the polymer and fibres are inherent non flammable. A limiting oxygen index of 38 percent can be measured. P84 can be used to temperatures up to 260 °C depending on the environment. Fibre Properties Features of the P84 polyimide fibres are the irregularly lobed cross-section being responsible for the high bulk of the fibres. The typical mechanical fibre data describe that P84 is rather a textile fibre with good knot and loop strength properties. Because of the low modulus and the high elongation P84 polyimide fibres are not destined for typical "reinforcing" applications as p-aramid or carbon fibres.

Message

P84® polyimide derived from aromatic dianhydrides and aromatic diisocyanates exhibits outstanding thermal stability. The polymer is non melting, has a glass transition temperature of 315°C. The fibres start to carbonize at temperatures beyond 370 °C. Due to the aromatic structure the polymer and fibres are inherent non flammable. A limiting oxygen index of 38 percent can be measured. P84 can be used to temperatures up to 260 °C depending on the environment.

Fibre Properties
Features of the P84 polyimide fibres are the irregularly lobed cross-section being responsible for the high bulk of the fibres. The typical mechanical fibre data describe that P84 is rather a textile fibre with good knot and loop strength properties. Because of the low modulus and the high elongation P84 polyimide fibres are not destined for typical "reinforcing" applications as p-aramid or carbon fibres.

General Information
Features	Aromatic Flame Retardant Good Thermal Stability
Forms	Fiber

Physical	Nominal Value	Unit
Density	1.41	g/cm³
Shrinkage - 10 minutes (240°C)	< 3.0	%

Additional Information	Nominal Value	Unit
Tenacity	4.29	g/denier

Mechanical	Nominal Value	Unit
Tensile Strain (Break)	30	%

Thermal	Nominal Value	Unit	Test Method
Glass Transition Temperature	315	°C	DSC

Flammability	Nominal Value	Unit
Oxygen Index	38	%

Resin Grade	Manufacturer	Category	Trademark
ACLAR® 22C (3 mil)	Honeywell	PCTFE	ACLAR®
Chemical Resources ABS1200	Chemical Resources, Inc.	ABS	Chemical Resources
Polifil® Nylon 730	The Plastics Group	Nylon 6	Polifil® Nylon
CERTENE™ 1320	Muehlstein	PS (HIPS)	CERTENE™
UBE Nylon 1013B	UBE Engineering Plastics, S.A.	Nylon 6	UBE Nylon